Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Markets
- Plastics & Elastomers End Uses
- Method of Application
- Substrates must be clean, dry, smooth, and free of sharp edges, fins, loose or foreign materials, oil, grease, and other materials that may damage the membrane.
- All roughened surfaces that can damage the membrane shall be repaired as specified to offer a smooth substrate.
- All surface voids greater than 1⁄4′′ (6.3 mm) wide shall be properly filled with an acceptable fill material.
- RubberGard MAX EPDM Membrane must be installed in accordance with current RubberGard specifications, details and workmanship requirements.
Properties
- Physical Form
- Typical Properties
Value | Units | Test Method / Conditions | |
Overall Thickness | 1.168 | mm | D 412 |
Coating Over Scrim | 0.559 | mm | D 7635 |
Breaking Strength | 969.7 | N | D 751 |
Elongation, Ultimate (fabric break, 15% MD) | 26.7 | % | D 751 |
Elongation, Ultimate (fabric break, 15% CD) | 35.2 | % | D 751 |
Tear Strength | 516 | N | D 751 |
Packaging & Availability
- Product Packaging
Membrane Thickness Width Length Weight 0.045" (1.14 mm) 10' (3.05 m) 100' (30.5 m) 0.32 lb/ft2 (1.5 kg/m2) 0.060" (1.52 mm) 10' (3.05 m) 100' (30.5 m) 0.42 lb/ft2 (2.1 kg/m2) 0.075′′ (1.91 mm) 10' (3.05 m) 100' (30.5 m) 0.55 lb/ft2 (2.7 kg/m2)
Storage & Handling
- Storage
- Store away from sources of punctures and physical damage.
- Assure that structural decking will support the loads incurred by material when stored on rooftop. The deck load limitations should be specified by the project designer.
- Store away from ignition sources as membrane will burn when exposed to open flame.
- Platinum PT membrane should be installed within one year after production. Store in original unopened packaging indoors at 60 °F to 80 °F (15.6 °C to 26.7 °C). Protect the tape portion from physical damage, and the Platinum PT membrane from puncture sources.