- Good mechanical properties
- Excellent chemical resistance
- Exceptional temperature resistanc
- Excellent electrical insulating properties
- High limiting oxygen index
- UV resistance - extremely non-adhesive
- Reduced friction & wear; Low friction behavior
- Suitable for food contact High degree of hydrophobicity
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Typical Application
Fluteck™ P1000 PTFE Standard Grade offers useful properties in various applications such as chemical resistance, thermal stability, cryogenic properties, low coefficient of friction, low surface energy, low dielectric constant, high volume and surface resistivity, and flame resistance. These properties allow the application of fluteck™ P1000 PTFE Standard Grade in several fields such as Chemical, Eletrical and Electronic, Petrochemical, Automotive, Mechanical, Medical, Aeronautics, Semiconductor and Food industry.
Properties
- Color
- Physical Properties
- Mechanical Properties
- Thermal Properties
| Value | Units | Test Method / Conditions | |
| Specific Gravity | 2.130 - 2.190 | g/cm³ | ASTM D792 |
| Water Absorption | 0.01 | % | ASTM D570 |
| Flamability | V - 0 | — | UL 94 |
| Value | Units | Test Method / Conditions | |
| Tensile Strength | min. 20 | MPa | ASTM D4894 |
| Elongation | min. 200 | % | ASTM D4894 |
| Hardness | min. 54 | Shore D | ASTM D2240 |
| Ball Hardness | min. 23 | MPa | ASTM D785 |
| Compression Strength (1% Deformation) | min. 4 | MPa | ASTM D695 |
| Deformation Under Load (140 kg/cm², 24hrs, 23°C) | 10 - 13 | % | ASTM D621 |
| Permanent Deformation (min. 24 Hrs, Relaxation 23°C) | 6 - 7.5 | % | ASTM D621 |
| Coefficient of Static Friction | 0.08 - 0.10 | — | ASTM D1894 |
| Coefficient of Dynamic Friction | 0.06 - 0.08 | — | ASTM D1894 |
| Wear Factor | 2.9 | — | ASTM D3702 |
| Wear Coefficient | 20000 - 25000 | kgmh | — |
| Value | Units | Test Method / Conditions | |
| Thermal Conductivity | 0.34 | W/mK | ASTM C177 |
| Coefficient of Linear Thermal Expansion (25°C - 100°C) | 12 - 15 | 10⁵/°C | ASTM D696 |
| Dielectric Strength | min. 30 | kV/mm | ASTM D149 |
| Volume Resistivity | 10¹¹ | Ohm-cm | ASTM D257 |
| Surface Resistivity | 10 | Ohm | ASTM D257 |
Regulatory & Compliance
- Certifications & Compliance
- Statement on suitability for contact with foodstuff
FDA Approved US Regulation
- Code of Federal regulation 21 CFR Ch.1; section 177.1550 Perfluorocarbon Resins of the Food and Drug Administration/US. EU Regulation
- EU 1935/2004 - 10/2011 on plastic materials and articles to come in contact with food.
Technical Details & Test Data
- Typical properties
Fluteck™ P1000 is a PTFE Standard Grade preferred for parts and components requiring very good mechanical properties. fluteckTMP1000 offers an excellent combination of properties typical of the fluoropolymer resins:
- Service Temperature : Fluteck™ P1000 offers excellent resistance to continuous service temperatures – working conditions from -100°C up to 250°C and, for limited periods, even to higher temperatures; Product’s low temperature resistance allows satisfactory performance down to –200°C.
- Chemical resistance : Fluteck™ P1000 offers high inertness towards nearly all known chemicals. Only attacked elemental alkali metals, chlorine trifluoride and elemental fluorine at high temperature and pressures might affect properties.
- Solvents resistance : Fluteck™ P1000 offers insoluble properties in all solvents up to temperatures as high as 300°C. Certain highly fluorinated oils only swell and dissolve PTFE at temperatures close to the crystalline melting point.
Storage & Handling
- Storage & Handling
Futeck™ P1000 PTFE Standard Grade can be stored for a long period of life and is exceptionally resistant to aging and weather conditions up to 10 years. Specific aging tests carried out on sample exposed to aging and atmospheric conditions, showed no changes in weight and volume. In case of semi-finished products, before processing or before the machining, it is advisable to store the material for 24 hours in the production area, preferable in a clean and dry place at a temperature of less than 25°C, preferably between 21-25°C. This is very important when room temperature is low; in such cases the material should be conditioned up to 72 hours in the production area in the recommended temperature range.