Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Color
- Flame Rating
- Physical Properties
- Mechanical Properties
- Thermal Properties
- Electrical Properties
- Flammability
- Processing Parameters
- Rheological Properties
Value | Units | Test Method / Conditions | |
Linear Mold Shrinkage | 0.40 - 0.7 | % | ISO 294-4 |
Value | Units | Test Method / Conditions | |
Tensile Strain (Yield, 23°C) | 2.4 | % | ISO 527 |
Tensile Strain (Yield, 23°C) | 44.0 | MPa | ISO 527 |
Tensile Modulus | 2300.0 | MPa | ISO 527 |
Nominal Strain at Break (23°C) | 12.0 | % | ISO 527 |
Flexural Modulus | 2500.0 | MPa | ISO 178 |
Flexural Strength | 65.0 | MPa | ISO 178 |
IZOD Notched Impact Strength (+23°C) | 22.0 | KJ/m2 | ISO 180/1eA |
IZOD Notched Impact Strength (-30°C) | 7.0 | KJ/ m2 | ISO 180/1eA |
Value | Units | Test Method / Conditions | |
Heat Distortion Temperature (Under 1.8 Mpa Load, HDT A) | 92.0 | °C | ISO 75 |
Heat Distortion Temperature (Under 0.45 MPa Load, HDT B) | 95.0 | °C | ISO 75 |
Vicat Softening Point (Under 9.8 N Load, Vicat A) | 95.0 | °C | ISO 306 |
Vicat Softening Point (Under 0.49 N Load, Vicat B) | 102.0 | °C | ISO 306 |
Value | Units | Test Method / Conditions | |
Volume Resistivity | 10000000000000.0 | Ω*m | IEC 60093 |
Surface Resistivity | 100000000000000.0 | Ω | IEC 60093 |
Electic Strength | 41.0 | kV/mm | IEC 60243 - |
Value | Units | Test Method / Conditions | |
Flammability Rate (0.8 mm thickness) | HB | — | UL94 |
Flammability Rate (1.6 mm thickness) | HB | — | UL94 |
Flammability Rate (3.2 mm thickness) | HB | — | UL94 |
Value | Units | Test Method / Conditions | |
Melt Temperature range | 220 - 260 | °C | ISO 294 |
Mold Temperature Range | 30 - 60 | °C | ISO 294 |
Drying Temperature | 80.0 | °C | — |
Drying Time | 2 - 4 | h | — |
Value | Units | Test Method / Conditions | |
Density | 1.04 | kg/m3 | ISO 1183 |
Water Absorption SatuRated (23°C) | 0.95 | % | ISO 62 |
Moisture Absorption Equilibrium (23°C 50% r.U) | 0.24 | % | ISO 62 |
Melt Volume Rate (220°C 10 kg) | 34.0 | cm3/10 min | ISO 1133 |
Regulatory & Compliance