Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Color
- Flame Rating
- Physical Properties
- Mechanical Properties
- Thermal Properties
- Electrical Properties
- Flammability
- Processing Parameters
- Rheological Properties
| Value | Units | Test Method / Conditions | |
| Melting Point (DSC) | 165.0 | °C | ISO 3146 |
| Value | Units | Test Method / Conditions | |
| Tensile Modulus | 5000.0 | MPa | ISO 527 - 2 |
| Tensile Stress Yield | 70.0 | MPa | ISO 527 - 2 |
| Strain at Break | 3.0 | % | ISO 527 - 2 |
| Flexural Modulus | 4700.0 | MPa | ISO 178 |
| Maximum Flexural Stress | 115.0 | MPa | ISO 178 |
| IZOD Notched Impact Strength (+23°C) | 14.0 | KJ/m2 | ISO 180/1eA |
| Value | Units | Test Method / Conditions | |
| Heat Distortion Temperature (Under 1.8 Mpa Load, HDT A) | 135.0 | °C | ISO 75 - 2 |
| Vicat Softening Point (Under 0.49 N Load, Vicat B) | 115.0 | °C | ISO 306 |
| Value | Units | Test Method / Conditions | |
| Volume Resistivity | 1.0e+15 | Ω*cm | IEC 60093 |
| Surface Resistivity | 1.0e+16 | Ω | IEC 60093 |
| Comparative Tracking Index | 600.0 | V | IEC 60112 |
| Value | Units | Test Method / Conditions | |
| Flammability Rate (0.8 mm thickness) | HB | - | UL94 |
| Flammability Rate (1.6 mm thickness) | HB | - | UL94 |
| Flammability Rate (3.2 mm thickness) | HB | - | UL94 |
| Oxygen Index | 21.0 | % | ISO 4589-1/-2 |
| Value | Units | Test Method / Conditions | |
| Melt Temperature | 210 - 250 | °C | CYLINDER |
| Melt Mold | 45 - 70 | °C | MOLD |
| Drying Temperature | 80.0 | °C | - |
| Dry Time | 2.0 | h | - |
| Value | Units | Test Method / Conditions | |
| Density | 1.13 | g/cm3 | ISO 1183 |
| Humidity Absorption | 0.04 | % | Similar ISO 62 |
| Melt Volume-Flow Rate (230°C 2.16kg) | 9.0 | °C | ISO 1133 |
| Molding Shrinkage (Parallel) | 0.25 - 0.45 | % | ISO 294-4 |
| Molding Shrinkage (Normal) | 0.75 - 0.1 | % | ISO 294-4 |
Regulatory & Compliance