Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Color
- Flame Rating
- Mechanical Properties
- Thermal Properties
- Electrical Properties
- Flammability
- Processing Parameters
- Rheological Properties
| Value | Units | Test Method / Conditions | |
| Tensile Modulus | 5000 - 5800 | MPa | ISO 527 - 2 |
| Stress at Break | 75.0 | MPa | ISO 527 - 2 |
| Strain at Break | 2.5 | % | ISO 527 - 2 |
| Flexural Modulus | 4800 - 5200 | MPa | ISO 178 |
| Maximum Flexural Stress | 120.0 | MPa | ISO 178 |
| IZOD Notched Impact Strength (+23°C) | 9.0 | KJ/m2 | ISO 180/1eA |
| Value | Units | Test Method / Conditions | |
| Heat Distortion Temperature (Under 1.8 Mpa Load, HDT A) | 145.0 | °C | ISO 75 - 2 |
| Vicat Softening Point (Under 0.49 N Load, Vicat B) | 130.0 | °C | ISO 306 |
| Value | Units | Test Method / Conditions | |
| Volume Resistivity | 100000000000000.0 | Ω*cm | IEC 60093 |
| Surface Resistivity | 1.0e+15 | Ω | IEC 60093 |
| Value | Units | Test Method / Conditions | |
| Flammability Rate (0.8 mm thickness) | HB | - | UL94 |
| Flammability Rate (1.6 mm thickness) | HB | - | UL94 |
| Flammability Rate (3.2 mm thickness) | HB | - | UL94 |
| Value | Units | Test Method / Conditions | |
| Melt Temperature | 210-255 | °C | CYLINDER |
| Mould Temperature | 45-70 | °C | MOULD |
| Drying Temperature | 80.0 | °C | - |
| Dry Time | 2.0 | h | - |
| Value | Units | Test Method / Conditions | |
| Density | 1.10 - 1.15 | g/cm3 | ISO 1183 |
| Humidity Absorption | 0.05 | % | Similar ISO 62 |
| Melt Flow Index | 4 - 7 | cm3/10min | ISO 1133 |
| Molding Shrinkage (Parallel) | 0.25 - 0.45 | % | ISO 294-4 |
| Molding Shrinkage (Normal) | 0.75 - 1.00 | % | ISO 294-4 |
| Melting Point (DSC) | 165.0 | °C | ISO 3146 |