Value | Units | Test Method / Conditions | |
Melting Point (DSC) | 166.0 | °C | ISO 3146 |
Value | Units | Test Method / Conditions | |
Tensile Modulus | 2900.0 | MPa | ISO 527 - 2 |
Stress at Break | 65.0 | MPa | ISO 527 - 2 |
Yield Strain | 9.0 | % | ISO 527 - 2 |
Strain at Break | 31.0 | % | ISO 527 - 2 |
Flexural Modulus | 2700.0 | MPa | ISO 178 |
Maximum Flexural Stress | 85.0 | MPa | ISO 178 |
IZOD Notched Impact Strength (+23°C) | 6.5 | KJ/m2 | ISO 180/1eA |
Value | Units | Test Method / Conditions | |
Heat Distortion Temperature (Under 1.8 Mpa Load, HDT A) | 95.0 | °C | ISO 75 - 2 |
Heat Distortion Temperature (Under 0.45 MPa Load, HDT B) | 157.0 | °C | ISO 75 - 2 |
Vicat Softening Point (Under 0.49 N Load, Vicat B) | 150.0 | °C | ISO 306 |
Value | Units | Test Method / Conditions | |
Volume Resistivity | 10000000000000.0 | Ω*cm | IEC 60093 |
Surface Resistivity | 10000000000000.0 | Ω | IEC 60093 |
Comparative Tracking Index | 600.0 | V | IEC 60112 |
Electric Strength | 40.0 | kV/mm | IEC 60243-1 |
Value | Units | Test Method / Conditions | |
Flammability Rate (0.8 mm thickness) | HB | — | UL94 |
Flammability Rate (1.6 mm thickness) | HB | — | UL94 |
Flammability Rate (3.2 mm thickness) | HB | — | UL94 |
Oxygen Index | 15.0 | % | ISO 4589-1/-2 |
Value | Units | Test Method / Conditions | |
Melt Temperature | 180 - 205 | °C | CYLINDER |
Melt Mold | 60 - 80 | °C | MOLD |
Drying Temperature | 80.0 | °C | — |
Dry Time | 3.0 | h | — |
Value | Units | Test Method / Conditions | |
Density | 1.41 | g/cm3 | ISO 1183 |
Humidity Absorption | 0.2 | % | Similar ISO 62 |
Water Absorption (23°C 50% r.U) | 0.6 | % | ISO 62 |
Melt Volume-Flow Rate (190°C 2.16 kg) | 9.0 | °C | ISO 1133 |
Molding Shrinkage (Parallel) | 2.2 | % | ISO 294-4 |
Molding Shrinkage (Normal) | 1.8 | % | ISO 294-4 |