Identification & Functionality
- Chemical Family
- Product Type
- Technologies
- Product Families
Features & Benefits
- Ready-to-Use Product Features
Applications & Uses
- Markets
- Applications
- Applications
Application
Components are to be mixed homogeneously (e.g. with high-speed mixer).
spraying-airless: in original viscosity after hardener addition
spraying-airmix: in original viscosity after hardener addition
spraying-high pressure: in original viscosity after hardener addition
Substrates
shot blasted steel, iron phosphatized steel, steel without pretreatment, zinc phosphate steel
Pretreatment
The substrate must be free of materials which prevent adhesion, e.g. oil, grease and tensids. According to the requirements we recommend to apply the suited chemical (e.g. phosphatizing, chromating) or / and mechanical (e.g. shot blasting) pretreatment.
Proposal for a coating systemsubtrate: shot blasted steeltop coat: EFDEDUR-UHS-Singlelayer UR1422GApplication temperature
above 10 °CDrying air drying at 20°Cdust dry: after 45 min. (degree of drying 1/ DIN EN ISO 9117-5)dry to touch: after 5 h (degree of drying 4/ DIN EN ISO 9117-5)dry to assambling: after 6 h (degree of drying 6/ DIN EN ISO 9117-5)complete dry: after 14 days (swinging beam hardness/ DIN EN ISO 1522)oven drying: possible up to 80°C (object temperature)Recoatability
With itself after previous cleaning, at any time possible
Cleaning of working equipment
EFD-Thinner 400500
Properties
- Special Remarks
Test condition
*Indication of the delivery viscosity according to DIN 53211:
DIN 53211 was withdrawn in October 1996. On request the value is available according to DIN EN ISO 2431.
The statements concerning efficiency, drying and caution labeling depend on color shade. The values mentioned in this data sheet are based on UR1422GL1504, vermilion hardening with HU0145.
All information is based on a standard climate 20/65 DIN 50014.
For the calculation of the practical consumption loss additions have to be considered. Indications to this are the practical experience and advices given in DIN 53220.
All information are based on our product knowledge and experience. To the application we have no direct influence. For further information please don’t hesitate to contact us. The information mentioned herein are reference values and are not given as specification.Consumption
calculated, after hardener addition
in original viscosity, without application loss240 to 250 g / m²
dry film thickness 90 μm
see „Special remarks”- Properties
Technical Physical Data Resin/ binder polyacrylic resin to be hardened with isocyanateTechnical Physical Data Gloss value
DIN 67530 and DIN EN ISO 2813glossy 71 to 85 angle 60°Technical Physical Data Original viscosity
DIN 53211*
without hardener50 to 70 Sek. / 4 mm cupTechnical Physical Data Mixing ratio
by weight8 : 1 Technical Physical Data Mixing ratio
by Volume parts4.75 : 1 Technical Physical Data Hardener
baseEFDEDUR-Hardener HU0145
polyisocyanateTechnical Physical Data Potlife
after hardener addition3 h / 20° Technical Physical Data Thinner EFD-Thinner 400500 or
EFD-Thinner 400474Technical Physical Data Density
after hardener addition
calculated1.65 g / ml + / - 0.1Technical Physical Data Solid content
after hardener addition
calculated80 % + / - 2 Technical Physical Data Solid content in volume
after hardener addition
calculated369 ml / kg + / - 20
Regulatory & Compliance
- Certifications & Compliance
Safety & Health
- Advise for Safety Protection and Protection of Health
The usual precautionery measures for ventilation as well as for personal protection are to be observed when handling painting materials. Detailled information about dangerous goods, safety data and recommendations concerning health protection and environment protection can be read in the corresponding safety data sheet.
Storage & Handling
- Storability
Approx. 12 month in original packings at an ambient temperature of 5 to 25 °C, in case the original packings are tightly closed. Opened packing must be used very shortly. The minimum storage stability of each batch is mentioned on the product label. A storage time beyond the mentioned date doesn´t necessarily mean that the material is unusable. In this case a check of the qualities which are important for the respective use is necessary.