Properties
- Flame Rating
- Flame Rating
- IEC 60695-11-10 V2
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Electrical Properties
- Flammability
Value | Units | Test Method / Conditions | |
Tensile Strength | 155 / - | MPa | ISO 527 |
Tensile Modulus | 9500 / - | MPa | ISO 527 |
Charpy notched impact strength (+23°) | 9 / - | kJ/m2 | ISO 179/1eA |
Ball indentation hardness | 240 / - | MPa | ISO 2039-1 |
Value | Units | Test Method / Conditions | |
Melt Volume Flow Rate - MVR (275°C/5.0 kg) | 40 | cm3/10min | ISO 1133 |
Molding Shrinkage - Paralell (60×60×2 mm) | 0 | % | ISO 294-4 |
Molding Shrinkage - Paralell (60×60×2 mm) | 1/1 | % | ISO 294-4 |
Density | 1.46 | g/cm3 | STANDARD ISO 1183 |
Value | Units | Test Method / Conditions | |
Delfection Temperature Under Load (1.8 MPa) | 170 | °C | ISO 75-1,-2 |
Temperature of deflection under load (1.80 Mpa) | 190 / * | °C | ISO 75-1/-2 |
Melting Point (DSC) | 221 | °C | ISO 11357-1 |
Vicat Softening Temperature (50 N) | 210 | °C | ISO 306 |
Melting temperature (10°C/min) | 221 / * | °C | ISO 11357-1/-3 |
Thickness tested | 1.6 / * | mm | — |
Vicat softening temperature | 195 / * | °C | ISO 306 |
Burning Behavior at 1.5 mm nominal thickness | V-2 / * | class | IEC 60695-11-10 |
Value | Units | Test Method / Conditions | |
Comparative Tracking Index - CTI | 325 | - | IEC 60112 |
Surface Resistivity | 1.00E+11 | ohm | STN 34 6460 |
Volume Resistivity | 100000000000.0 | ohm.m | IEC 60093 |
Value | Units | Test Method / Conditions | |
Flammability - Glow Wire Test | 950 | °C | IEC-60695-2-12 |