BAI YUN PPO Solar Panel Silicone Sealant SMG533 Silicone Encapsulant For Solar Cells

Identification & Functionality

Chemical Family: Silicones
Product Type: 1K (1 component) Sealant,
Encapsulant,
Potting Compound
Technologies: Ready-to-Use Products
Product Families: Ready-to-Use Products — Adhesives & Sealants
Caulks & Sealants,
Encapsulants
Origin: China.

Features & Benefits

Ready-to-Use Product Features: Fast Curing,
Good Adhesion,
Maintains Elasticity,
Ozone Resistant,
UV Resistant,
Water Resistant
Features: One component, neutral alkoxy curing silicone sealant, fast curing

Easy to use, good aging resistance, water resistance, ozone resistance, UV resistance

It has excellent adhesion to the photovoltaic panel materials, including solar panel aluminum frame, glass, TPT/TPE, etc.

Excellent durability test: Pass the thermal shock test (-40-85℃), damp heat test (85℃/85%RH/1000 h) and other related aging tests. Will not soften or degrade after curing, and always maintain good elasticity

Have complete certification qualifications and passed SGS, UL, TUV certification.

Applications & Uses

Markets: Consumer Goods,
Electrical & Electronics
Applications: Consumer Goods — Appliances & Electronics
Electrical & Electronics — Packaging & Assembly
Adhesives & Sealants
Applications: Used for PV modules frame sealing, junction box adhesion and rail bonding

Solar panel aluminum frame and glass,

TPT/TPE Backsheet
Instructions: The surface of substrate must be clean and dry, preferred solvents including isopropanol, acetone, and methyl ethyl ketone.For some special substrates, such as PP and PTEE, needed chemical corrosion or plasma treatment to meet bonding effect.

Match pneumatic dispenser or machine to meet dispensing process.

After skin formation, cure continues inward from the surface. In 24 hours (at 25℃and 50% relative humidity). SMG533-S will cure to a depth of about 3.3 mm. The deep-seated part, especially the part that has limit contact with air has longer curing time. Similarly curing time would extend in low-temperature condition.

Properties

	Value	Units	Test Method / Conditions
Appearance (Before Curing)	White or gray paste	—	Eye-measurement
Density (Before Curing)	1.4	g/cm3	GB/T 13354-1992
Working Time (25℃, 50% Rh, Before Curing)	12.0	min	GB/T13477.5-20
Extrusion Rate (Before Curing)	52,0.5,25,3	g/min,MPa,℃,mm	—
Hardness (After Total Curing)	41.0	Shore A	GB/T 531-1999
Tensile Strength (After Total Curing)	2.5	MPa	GB/T 528-1998
Elongation At Break (Cured-After 21 Days At 23°C (73°F) And 50% Rh)	450.0	%	GB/T 528-1998
Shear Strength (Cured-After 21 Days At 23°C (73°F) And 50% Rh)	14.0	—	GB/T 528-1998
Volume Resistivity (After Total Curing)	1.0×10^15	Ω.cm	GB/T 1962-92
Dielectric Strength (After Total Curing)	16.0	KV/mm	GB/T 1408.1-1999
Working Temperature (After Total Curing)	-50 to 220	°C	—

Regulatory & Compliance

Safety & Health

Attention: Far away from children by storage.

In case of contact with shin, wash with water.

If accident contact with eyes, flush with plenty of water immediately.

Proposed use in a well-ventilated place.

Packaging & Availability

Packaging Type: Cartridges,
Sausages
Packing: 310 ml/Cartridge; 400ml /Cartridge; 235Kg/55 gallons of pail

Minimum Order Quantity: Cartridge / Sausage Packaging 1000PCS

Delivery Time: 7-14days

Supply Ability: Cartridge / Sausage Packaging 1000000PCS/month; Drum Packaging 10000 Kits / month

Package: 24 Pcs Per Box/ 64 Boxes Per Pallet

BAI YUN® PPO Solar Panel Silicone Sealant SMG533 Silicone Encapsulant For Solar Cells