Flame retardant masterbatch based on melamine cyanurate with a total load of 50% active substance, which is designed for PA6, PA66, and PA 12.
Applications & Uses
- Markets
- Compatible Polymers & Resins
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Application
Compared with powder flame retardants, MB50 has better dispersion and higher production efficiency, and can be used directly mixing with resin for injection or extrusion molding. MB50 can also be added to resin for compounding process, which has advantages in dust free, easy to feed, and excellent dispersion. JLS-MB50 is especially suitable for PA6, PA66, PA12 products, such as corrugated pipe. JLS-MB50 can also be used for glass fiber reinforced nylon.
- Guidelines for use
PA6 UL94V-O(O.8mm) 28-30 wt%
UL94V-O(1.6mm) 24-26 wt0/0PA66 UL94V-O(O.8mm) 26-28 wt%
UL94V-O(1.6mm) 22-24wt%PA12 UL94V-O(O.8mm) 30-34 Wt%
GFPA 6, 66 UL94V-2(O.8mm) 30-40wt%
It can be processed at 210-2750. Pre-dry is not necessary when the package is in good condition. But after open or on moisture, pre-dry under 9(W950C for 2 hours is required.
Properties
- Physical Form
- Appearance
- Uniform particles
- Typical Properties
| Value | Units | Test Method / Conditions | |
| Flame retardant content | 50 | % | — |
| Water content | max. 0.2 | % | — |
| Density at 25°C | approx. 1.33 | g/cm3 | — |
Regulatory & Compliance
- Certifications & Compliance
- Regulatory compatibility
REACH, RoHS.