- Melt Temperature : 140 ~ 170℃
- Blow-up Ratio : 2 ~ 3
- Optimum Gage Range : 0.025 ~ 0.1 mm
- Additves
- Slip agent, Anti-block agent
Properties
- Physical Form
- Physical Properties
- Film Properties
Value | Units | Test Method / Conditions | |
Melt Index | 3 | g/10min | ASTM D1238 |
Density | 0.921 | g/cc | ASTM D1505 |
Vicat Softening Point | 88 | ˚C | ASTM D1525 |
Melting Point | 110 | ˚C | HCC Method |
Tensile Strength at Break | 110 | kg/cm2 | ASTM D638 |
Elongation at Break | 650 | % | ASTM D638 |
Brittleness Temperature, F0 | max. -76 | ˚C | ASTM D746 |
Value | Units | Test Method / Conditions | |
Film Thickness | 0.03 | mm | HCC Method |
Tensile Strength at Break (MD) | 230 | kg/cm2 | ASTM D882 |
Tensile Strength at Break (TD) | 180 | kg/cm2 | ASTM D882 |
Elongation at Break (MD) | 350 | % | ASTM D882 |
Elongation at Break (TD) | 550 | % | ASTM D882 |
Tensile Tear Strength (MD) | 90 | kg/cm | ASTM D1004 |
Tensile Tear Strength (TD) | 85 | kg/cm | ASTM D1004 |
Dart Impact Strength | 85 | g | ASTM D1709 |
Haze | 4 | % | ASTM D1003 |