Epoxy Primer Overview
Epox-Zen™ Epoxy Primers are a substantial upgrade from conventional alkyd primers and provide durable protection over ferrous and non-ferrous metals, specific FRPs and composites. Epox-Zen™ Epoxy Primers should be top coated with epoxy or polyurethane finishes to achieve the ultimate in protection and durability.
Epoxy Primary Characteristics
Epox-Zen™ Epoxy Primers are engineered to offer the finest corrosion protection, chemical resistance, adhesion and topcoat hold-out. Epox-Zen™ Epoxy Primers also dry quickly, enabling quick topcoat application.
Applications & Uses
- Markets
- Applications
- Compatible Substrates & Surfaces
- Best For
- Agriculture, Construction, Material Handling Equipment
- Heavy gage substrate with aggressive blast profiles
Properties
- Typical Properties
| Value | Units | Test Method / Conditions | |
| Optimum Dry Film Thickness | 2.0 | mils | — |
| Gloss (60°) | 0-10 | — | — |
| Mix Ratio (Part A:Part B) | 4:1 | — | — |
| VOC | max. 3.5 | lbs/gal | — |
| ls HAPs Free Formula | Yes | — | — |
| 30 Minute Induction Time Needed | Yes | — | — |
| Pot Life (Before 50% Increase in Viscosity) | 8.0 | hours | — |
| Wet Film Sag Resistance | 12.0 | mils | — |
| Air Dry to Touch | 30.0 | minutes | — |
| Air Dry to Handle (Hard Dry) | 4.0 | hours | — |
| Air Dry Full Cure | 2.0 | Weeks | — |
| Force Cure - Ambient Flash Time Before Baking | 10.0 | minutes | — |
| Force Cure - Recommended Cure Time (180°) | 10.0 | minutes | — |
| Minimum Dry Time Before Product can be Sanded (After Bake) | 16.0 | hours | — |
| Minimum Dry Time Before Topcoat Application (After Bake) | 15.0 | minutes | — |
| Maximum Dry Time Before Topcoat Application | 48.0 | hours | — |
| Corrosion Resistance | Excellent | — | — |