Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Markets
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Flame Rating
- Flame Rating
- UL 94 5VA
- Physical Properties
- Thermal Properties
- Electrical Properties
- Flammability
- Processing Parameters
| Value | Units | Test Method / Conditions | |
| Mold Shrinkage - Cross Flow (-30°C) | 53 | x10-6mm/mm/°C | TMA |
| Mold Shrinkage - Flow (-30°C) | 24 | x10-6mm/mm/°C | TMA |
| Water Absorption (24h, 50% RH) | 0.01 | % | ISO 62 |
| Density | 1.32 | g/cm3 | ISO 1183/A |
| Glass Content | 22 | wt% | — |
| Value | Units | Test Method / Conditions | |
| Linear Thermal Expansion Coefficient - Cross Flow | 0.5–0.7 | % | Idemitsu Method |
| Linear Thermal Expansion Coefficient - Flow | 0.2–0.4 | % | Idemitsu Method |
| Deflection Temperature Under Load (1.8 MPa) | 230 | — | ISO 75 A |
| Deflection Temperature Under Load (0.45 MPa) | 265 | — | ISO 75 B |
| Value | Units | Test Method / Conditions | |
| Arc Resistance | 5 | PLC level | ASTM D495 |
| Comparative Tracking Index - CTI | 1 | PLC level | IEC 60112 Solution A |
| Dielectric Constant (1 MHz) | 3 | - | ASTM D 150 |
| Dissipation Factor (1 MHz) | 0.001 | - | ASTM D 150 |
| RTI Mechanical with Impact (Imp) | 120 | °C | UL 746B |
| RTI Mechanical Without Impact (Str) | 120 | °C | UL 746B |
| Dielectric Strength | 35 | kV/mm | IEC 60243-1 |
| RTI Elec | 125 | °C | UL 746B |
| Volume Resistivity | min. 1E+16 | Ω·cm | ASTM D257 |
| Value | Units | Test Method / Conditions | |
| Flammability (1.5 mm) | V0 | Class | UL 94 |
| Flammability (2.2 mm) | 5VA | Class | UL 94 |
| High Ampere Arc Resistance - HAI (1.5 mm) | 0 | PLC level | UL 746A |
| High Ampere Arc Resistance - HAI (3.0 mm) | 0 | PLC level | UL 746A |
| High Voltage Arc Tracking Rate - HVTR | 0 | PLC level | UL 746A |
| Hot Wire Ignition - HWI (1.5 mm) | 1 | PLC level | UL 746A |
| Hot Wire Ignition - HWI (3.0 mm) | 0 | PLC level | UL 746A |
| Value | Units | Test Method / Conditions | |
| Pre-drying Timings | 3.0 - 5 | h | — |
| Pre-drying Temperature | 120 | °C | — |
| Mold Temperature | 130 - 155 | °C | — |
| Melt Temperature | 280 - 310 | °C | — |