Value | Units | Test Method / Conditions | |
Tensile Modulus | 4600 | MPa | ASTM D 638 |
Charpy Notched Impact Strength (23°C) | 7 | kJ/m2 | ISO 179-1/1eA |
Charpy Notched Impact Strength (-20°C) | 4.5 | kJ/m2 | ISO 179/1eA |
Tensile Stress at Yield (50 mm/min) | 65 | MPa | ISO 527-2/1A |
Tensile Strain at Yield (50 mm/min) | 3 | % | ISO 527-1, -2 |
Value | Units | Test Method / Conditions | |
Density (23°C) | 1.05 | g/cm3 | ISO 1183 |
Melt Mass Flow Rate - MFR (230°C/2.16kg) | 16 | g/10min | ISO 1133 |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature - HDT/B (0.45 MPa) | 155 | °C | ISO 75 |
Value | Units | Test Method / Conditions | |
Recommended Processing Parameters | Injection Molding | - | — |
Barrel Temperatures | 190 to 230 | °C | — |
Injection Speed | Intermediate | - | — |
Polymer Melt Temperature | 210 to 240 | °C | — |
Mold Temperature | 10 to 50 | °C | — |
Hold Pressure | 50 – 100 % of injection pressure | - | — |
Value | Units | Test Method / Conditions | |
Abbreviated Term | PP-H GF20 | - | ISO 1043 |