Properties
- Color
- Physical Form
- Physical Properties
- Mechanical Properties
- Thermal Properties
- Flammability
- Other Properties
- Processing Information (Injection Molding)
- Additional Information
| Value | Units | Test Method / Conditions | |
| Density (23°C) | 1.04 | g/cm3 | ISO 1183 |
| Molding Shrinkage - Across Flow | 0.8 | % | ASTM D955 |
| Melt Mass Flow Rate - MFR (230°C/2.16kg) | 8 | g/10 min | ISO 1133 |
| Molding Shrinkage - Parallel | 1 | % | ISO 294-4, 2577 |
| Melt Volume Flow Rate - MVR (230°C/2.16kg) | 9 | ml/10 min | ISO 1133 |
| Value | Units | Test Method / Conditions | |
| Tensile Stress at Yield (50 mm/min) | 34 | MPa | ISO 527-2 |
| Tensile Strain at Yield (50 mm/min) | 5 | % | ISO 527-2/1A |
| Charpy Impact Strength (23°C) | 46 | kJ/m2 | ISO 179/1eU |
| Charpy Notched Impact Strength (-30°C) | 1.5 | kJ/m2 | ISO 179/1eA |
| Tensile Modulus (1 mm/min) | 2650 | MPa | ISO 527-1,-2 |
| Nominal Tensile Strain at Break | 23 | % | ISO 527-1,-2 |
| Charpy Impact Strength (-30°C) | 18 | kJ/m2 | ISO 179/1eU |
| Charpy Notched Impact Strength (23°C) | 3.4 | kJ/m2 | ISO 179/1eA |
| Flexural Modulus (2 mm/min) | 2730 | MPa | ISO 178 |
| Value | Units | Test Method / Conditions | |
| Melting Temperature (DSC) | 162 | °C | ISO 11357-3 |
| Heat Deflection Temperature - HDT/B (0.45 MPa) | 125 | °C | ISO 75-2 |
| Vicat Softening Temperature (A120) | - | °C | ISO 306 |
| Vicat Softening Temperature (B120) | - | °C | ISO 306 |
| Heat Deflection Temperature - HDT/A (1.8 MPa) | 71 | °C | ISO 75-1,-2 |
| Value | Units | Test Method / Conditions | |
| Automotive Materials (thickness d ≥ 1 mm) | + | - | FMVSS 302 |
| Value | Units | Test Method / Conditions | |
| Ash Content (600°C) | 19 | % | ISO 3451-1/A |
| Value | Units | Test Method / Conditions | |
| Recommended Processing Parameters | Injection Molding | - | — |
| Mold Temperature | 20 to 50 | °C | — |
| Injection Speed | Intermediate | - | — |
| Barrel Temperatures | 190 to 250 | °C | — |
| Polymer Melt Temperature | 210 to 260 | °C | — |
| Hold Pressure | as low as possible – to avoid sink marks | - | — |
| Value | Units | Test Method / Conditions | |
| Abbreviated Term | PPH TD 20 | - | ISO 1043 |