Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Color
- Physical Properties
- Mechanical Properties
- Thermal Properties
- Flammability
- Processing Information (Injection Molding)
- Additional Information
| Value | Units | Test Method / Conditions | |
| Density (23°C) | 1.04 | g/cm3 | ISO 1183 |
| Melt Mass Flow Rate - MFR (230°C/2.16kg) | 12 | g/10min | ISO 1133 |
| Value | Units | Test Method / Conditions | |
| Charpy Notched Impact Strength (23°C) | 3 | kJ/m2 | ISO 179/1eA |
| Tensile Stress at Yield (50 mm/min) | 32 | MPa | ISO 527-2/1A |
| Tensile Strain at Break (50 mm/min) | 12 | % | ISO 527 |
| Tensile Strain at Yield (50 mm/min) | 4.5 | % | ISO 527 |
| Flexural Modulus (2 mm/min) | 2700 | MPa | ISO 178 |
| Tensile Modulus (1 mm/min) | 2750 | MPa | ISO 527-1,-2 |
| Tensile Stress at Break (50 mm/min) | 26 | MPa | ISO 527-1,-2 |
| Flexural Strength (1A/2) | 44 | MPa | ISO 178 |
| Value | Units | Test Method / Conditions | |
| Heat Deflection Temperature - HDT/A (1.8 MPa) | 62 | °C | ISO 75-1,-2 |
| Heat Deflection Temperature - HDT/B (0.45 MPa) | 118 | °C | ISO 75 |
| Vicat Softening Temperature (A) | 153 | °C | ISO 306 |
| Vicat Softening Temperature (B) | 101 | °C | ISO 306 |
| Value | Units | Test Method / Conditions | |
| Automotive Materials (thickness d ≥ 1 mm) | - | - | FMVSS 302 |
| Value | Units | Test Method / Conditions | |
| Recommended Processing Parameters | Injection Molding | - | — |
| Barrel Temperatures | 190 to 230 | °C | — |
| Mold Temperature | 20 to 50 | °C | — |
| Injection Speed | Intermediate | - | — |
| Polymer Melt Temperature | 210 to 240 | °C | — |
| Hold Pressure | 30 – 100% of injection pressure | - | — |
| Value | Units | Test Method / Conditions | |
| Abbreviated Term | PP-H TD 20 | - | ISO 1043 |