Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Color
- Physical Form
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Flammability
- Processing Information (Injection Molding)
- Additional Information
| Value | Units | Test Method / Conditions | |
| Flexural Strength | 81 | MPa | ASTM D 790 |
| Flexural Modulus | 2900 | MPa | ASTM D 790 |
| Tensile Modulus | 3050 | MPa | ASTM D638 |
| Charpy Notched Impact Strength (23°C) | 6.3 | kJ/m2 | ISO 179/1eA |
| Tensile Stress at Break (50 mm/min) | 51 | MPa | ISO 527 |
| Tensile Strain at Yield (50 mm/min) | 3.6 | % | ISO 527 |
| Tensile Stress at Yield (50 mm/min) | 53 | MPa | ISO 527-1,-2 |
| Tensile Strain at Break (50 mm/min) | 5.3 | % | ISO 527-1,-2 |
| Charpy Notched Impact Strength (-20°C) | 3.4 | kJ/m2 | ISO 179/1eA |
| Value | Units | Test Method / Conditions | |
| Density (23°C) | 0.97 | g/cm3 | ISO 1183-1/A |
| Melt Mass Flow Rate - MFR (230°C/2.16kg) | 5.5 | g/10min | ISO 1133 |
| Molding Shrinkage | 1.0± 0.2 | % | ISO 294-4 |
| Value | Units | Test Method / Conditions | |
| Heat Deflection Temperature - HDT/B (0.45 MPa) | 151 | °C | ISO 75-1,-2 |
| Value | Units | Test Method / Conditions | |
| Burning Behaviour (d=3.2 mm) | max. 80 | mm/min | FMVSS |
| Value | Units | Test Method / Conditions | |
| Recommended Processing Parameters | Injection Molding | - | — |
| Barrel Temperatures | 190 to 230 | °C | — |
| Injection Speed | Intermediate | - | — |
| Polymer Melt Temperature | 210 to 240 | °C | — |
| Mold Temperature | 10 to 50 | °C | — |
| Hold Pressure | 50 – 100 % of injection pressure | - | — |
| Value | Units | Test Method / Conditions | |
| Abbreviated Term | PP-H GF10 | - | ISO 1043 |