Enhanced TDS
Knowde-enriched technical product data sheet
Identification & Functionality
- Additives Included
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Color
- Flame Rating
- Flame Rating
- UL 94 V2
- Physical Properties
Value Units Test Method / Conditions Density (23°C) 0.92 g/cm3 ASTM D1505 Melt Mass Flow Rate - MFR (230°C/2.16kg) 6 g/10min ISO 1133 - Mechanical Properties
Value Units Test Method / Conditions Tensile Strain at Yield (50 mm/min) 9 % ISO 527-2/1A Tensile Stress at Yield (50 mm/min) 34 MPa ISO 527-2 Charpy Notched Impact Strength (-20°C) 1.5 kJ/m2 ISO 179/1eA Charpy Notched Impact Strength (23°C) 4.5 kJ/m2 ISO 179/1eA Tensile Modulus (2 mm/min) 1500 MPa ISO 527-1,-2 Flexural Modulus (2 mm/min) 1500 MPa ISO 178 - Thermal Properties
Value Units Test Method / Conditions Heat Deflection Temperature - HDT/B (0.45 MPa) 96 °C ISO 75-1,-2 Heat Deflection Temperature - HDT/A (1.8 MPa) 48 °C ISO 75-1,-2 - Flammability
Value Units Test Method / Conditions Burning Behaviour (d=1.6 mm) V-2 Class UL-94 - Processing Information (Injection Molding)
Value Units Test Method / Conditions Recommended Processing Parameters Injection Molding - - Injection Speed Intermediate - - Hold Pressure 30 – 100 % of actual injection pressure - - Mold Temperature 10 to 50 °C - Barrel Temperatures 190 to 240 °C - Polymer Melt Temperature 210 to 250 °C - - Additional Information
Value Units Test Method / Conditions Abbreviated Term PPH FR - ISO 1043