INNOPOL® CS 1-5140 LH

Identification & Functionality

Chemical Family

Polyolefins,

Polypropylenes (PP)

Fillers Included

Talc

Polymer Name

Polypropylene Homopolymer (HPP)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Basic Thermoplastics

Polyolefins

Features & Benefits

Materials Features

Good Processability,

High Stiffness,

Homopolymer

Applications & Uses

Markets

Automotive & Transportation,

Electrical & Electronics

Applications

Automotive & Transportation — Automotive

Exterior & Body,

Interior,

Other Automotive Applications,

Powertrain & UTH

Electrical & Electronics — Parts & Components

Housings & Enclosures

Plastics & Elastomers End Uses

Automotive Applications,

Automotive Exterior Parts,

Automotive Interior Parts,

Automotive Under The Hood,

Housings

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Color

Natural

Flame Rating

UL 94 HB

Physical Form

Solid

Flame Rating

UL 94 HB

Physical Properties

	Value	Units	Test Method / Conditions
Density (23°C)	1.22	g/cm3	ISO 1183
Melt Volume Flow Rate - MVR (230°C/5kg)	15	cm3/10 min	ISO 1133

Mechanical Properties

	Value	Units	Test Method / Conditions
Charpy Notched Impact Strength (23°C)	3.5	kJ/m2	ISO 179/1eA
Charpy Impact Strength (23°C)	30	kJ/m2	ISO 179/1eU
Tensile Stress at Yield (50 mm/min)	31	MPa	ISO 527-2/1A
Flexural Modulus (2 mm/min)	4100	MPa	ISO 178
Tensile Strain at Yield (50 mm/min)	3.6	%	ISO 527
Charpy Impact Strength (-30°C)	13	kJ/m2	ISO 179/1eU
Tensile Modulus (1 mm/min)	4000	MPa	ISO 527-1,-2
Nominal Tensile Strain at Break	7	%	ISO 527-1,-2
Charpy Notched Impact Strength (-30°C)	1.6	kJ/m2	ISO 179/1eA

Thermal Properties

	Value	Units	Test Method / Conditions
Vicat Softening Temperature (B120)	93	°C	ISO 306
Heat Deflection Temperature - HDT/B (0.45 MPa)	133	°C	ISO 75-1,-2
Vicat Softening Temperature (A120)	156	°C	ISO 306
Heat Deflection Temperature - HDT/A (1.8 MPa)	79	°C	ISO 75-1,-2

Flammability

	Value	Units	Test Method / Conditions
Burning Behaviour (d=3.2 mm)	HB	Class	UL-94

Other Properties

	Value	Units	Test Method / Conditions
Ash Content (600°C)	37	%	ISO 3451-1/A

Processing Parameters

	Value	Units	Test Method / Conditions
Polymer Melt Temperature	230 to 250	°C	—
Mold Temperature	10 to 50	°C	—
Injection Speed	Slow or Intermediate	-	—
Hold Pressure	50 – 100 % of actual injection pressure	-	—
Barrel Temperatures	190 to 240	°C	—

Additional Information

	Value	Units	Test Method / Conditions
Abbreviated Term	PP-H TD40	-	ISO 1043

Regulatory & Compliance

Certifications & Compliance

UL 94