Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
Applications & Uses
- Plastics & Elastomers Processing Methods
Properties
- Color
- Physical Properties
- Mechanical Properties
- Thermal Properties
- Processing Information (Injection Molding)
- Additional Information
Value | Units | Test Method / Conditions | |
Density (23°C) | 1.04 | g/cm3 | ISO 1183 |
Melt Mass Flow Rate - MFR (230°C/2.16kg) | 5 | g/10min | ISO 1133 |
Value | Units | Test Method / Conditions | |
Charpy Notched Impact Strength (-20°C) | 6 | kJ/m2 | ISO 179/1eA |
Charpy Notched Impact Strength (23°C) | 9 | kJ/m2 | ISO 179/1eA |
Tensile Stress at Yield (50 mm/min) | 70 | MPa | ISO 527 |
Flexural Strength (2 mm/min) | 105 | MPa | ISO 178 |
Flexural Modulus (2 mm/min) | 4400 | MPa | ISO 178 |
Tensile Strain at Break (50 mm/min) | 4 | % | ISO 527-1,-2 |
Tensile Modulus (2 mm/min) | 4500 | MPa | ISO 527-1,-2 |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature - HDT/B (0.45 MPa) | 155 | °C | ISO 75 |
Heat Deflection Temperature - HDT/A (1.8 MPa) | 138 | °C | ISO 75-1,-2 |
Vicat Softening Temperature (A120) | 160 | °C | ISO 306 |
Vicat Softening Temperature (B120) | 125 | °C | ISO 306 |
Value | Units | Test Method / Conditions | |
Recommended Processing Parameters | Injection Molding | - | — |
Injection Speed | Intermediate | - | — |
Mold Temperature | 10 to 50 | °C | — |
Barrel Temperatures | 190 to 240 | °C | — |
Polymer Melt Temperature | 210 to 250 | °C | — |
Hold Pressure | 50 – 100 % of injection pressure | - | — |
Value | Units | Test Method / Conditions | |
Abbreviated Term | PPH GF20 | - | ISO 1043 |