Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Plastics & Elastomers Processing Methods
Properties
- Color
- Physical Properties
- Mechanical Properties
- Thermal Properties
- Processing Information (Injection Molding)
- Additional Information
| Value | Units | Test Method / Conditions | |
| Density (23°C) | 1.21 | g/cm3 | ISO 1183 |
| Molding Shrinkage - Normal | 0.7 | % | ISO 294-4, 2577 |
| Molding Shrinkage - Parallel | 0.2 | % | ISO 294-4, 2577 |
| Melt Mass Flow Rate - MFR (230°C/2.16kg) | 3.5 | g/10 min | ISO 1133 |
| Value | Units | Test Method / Conditions | |
| Tensile Strain at Yield (50 mm/min) | 2.7 | % | ISO 527 |
| Flexural Modulus (2 mm/min) | 8500 | MPa | ISO 178 |
| Tensile Strain at Break (50 mm/min) | 4 | % | ISO 527-1,-2 |
| Tensile Stress at Yield (50 mm/min) | 104 | MPa | ISO 527-1,-2 |
| Tensile Stress at Break (50 mm/min) | 101 | MPa | ISO 527-1,-2 |
| Tensile Modulus (1mm/min) | 8700 | MPa | ISO 527-1,-2 |
| Charpy Notched Impact Strength (1eA, 23°C) | 12 | kJ/m2 | ISO 179/1eA |
| Charpy Notched Impact Strength (1eA, -20°C) | 10.5 | kJ/m2 | ISO 179/1eA |
| Charpy Impact Strength (1eU, 23°C) | 52 | kJ/m2 | ISO 179/1eA |
| Charpy Impact Strength (1eU, -20°C) | 51 | kJ/m2 | ISO 179/1eA |
| Flexural Strength (2 mm/min) | 154 | MPa | ISO 178 |
| Value | Units | Test Method / Conditions | |
| Vicat Softening Temperature (A120) | 163 | °C | ISO 306 |
| Vicat Softening Temperature (B120) | 138 | °C | ISO 306 |
| Heat Deflection Temperature (0.45 MPa) | 159 | °C | ISO 75-1,-2 |
| Heat Deflection Temperature (1.8 Mpa) | 149 | °C | ISO 75-1,-2 |
| Value | Units | Test Method / Conditions | |
| Recommended Processing Parameters | Injection Molding | - | — |
| Polymer Melt Temperature | 230 to 250 | °C | — |
| Injection Speed | Intermediate | - | — |
| Hold Pressure | 50 – 100 % of actual injection pressure | - | — |
| Barrel Temperatures | 190 to 250 | °C | — |
| Mold Temperature | 25 to 50 | °C | — |
| Value | Units | Test Method / Conditions | |
| Abbreviated Term | PP-H GF40 | - | ISO 1043 |