Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Plastics & Elastomers Processing Methods
Properties
- Color
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Processing Information (Injection Molding)
- Additional Information
| Value | Units | Test Method / Conditions | |
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m2 | ISO 179/1eA |
| Charpy Impact Strength (23°C) | 40 | kJ/m2 | ISO 179/1eU |
| Charpy Notched Impact Strength (-20°C) | 11 | kJ/m2 | ISO 179 |
| Tensile Stress at Yield (50 mm/min) | 114 | MPa | ISO 527-1,-2 |
| Tensile Strain at Yield (50 mm/min) | 2 | % | ISO 527-1,-2 |
| Tensile Strain at Break (50 mm/min) | 3.1 | % | ISO 527-1,-2 |
| Tensile Modulus (1mm/min) | 12000 | MPa | ISO 527-1,-2 |
| Charpy Impact Strength (-20°C) | 40 | kJ/m2 | ISO 179/1eU |
| Flexural Strength (2 mm/min) | 171 | MPa | ISO 178 |
| Flexural Modulus (1A/2 mm) | 12000 | MPa | ISO 178 |
| Value | Units | Test Method / Conditions | |
| Melt Mass Flow Rate - MFR (230°C/2.16kg) | 3 | g/10min | ISO 1133 |
| Density (23°C) | 1.40 | g/cm3 | ISO 1183 |
| Value | Units | Test Method / Conditions | |
| Heat Deflection Temperature - HDT/A (1.8 MPa) | 148 | °C | ISO 75-1/-2 |
| Heat Deflection Temperature - HDT/B (0.45 MPa) | 158 | °C | ISO 75-1,-2 |
| Vicat Softening Temperature (A120) | 163 | °C | ISO 306 |
| Value | Units | Test Method / Conditions | |
| Recommended Processing Parameters | Injection Molding | - | — |
| Injection Speed | Intermediate | - | — |
| Mold Temperature | 10 to 50 | °C | — |
| Hold Pressure | 50 – 100 % of actual injection pressure | - | — |
| Barrel Temperatures | 190 to 240 | °C | — |
| Polymer Melt Temperature | 210 to 250 | °C | — |
| Value | Units | Test Method / Conditions | |
| Abbreviated Term | PPH GF55 | - | ISO 1043 |