Properties
- Color
- Physical Properties
- Mechanical Properties
- Thermal Properties
- Processing Information (Injection Molding)
- Additional Information
| Value | Units | Test Method / Conditions | |
| Melt Volume Flow Rate - MVR (230°C/5 kg) | 8.5 | cm3/10 min | ISO 1133 |
| Density (23°C) | 1.13 | g/cm3 | ISO 1183 |
| Melt Mass Flow Rate - MFR (230°C/2.16kg) | 2 | g/10min | ISO 1133 |
| Melt Mass Flow Rate - MFR (230°C/5 kg) | 8.2 | g/10 min | ISO 1133 |
| Melt Volume Flow Rate - MVR (230°C/2.16kg) | 2.2 | cm3/10 min | ISO 1133 |
| Value | Units | Test Method / Conditions | |
| Flexural Modulus (2 mm/min) | 6800 | MPa | ISO 178 |
| Tensile Modulus (1 mm/min) | 6500 | MPa | ISO 527 |
| Tensile Strain at Break (50 mm/min) | 5 | % | ISO 527 |
| Tensile Stress at Yield (50 mm/min) | 96 | MPa | ISO 527-1,-2 |
| Flexural Strength (2 mm/min) | 135 | MPa | ISO 178 |
| Charpy Notched Impact Strength (23°C, A) | 14 | kJ/m2 | ISO 180 |
| Charpy Notched Impact Strength (-20°C, A) | 11 | kJ/m2 | ISO 180 |
| Charpy Unnotched Impact Strength (1eU, 23°C) | 55 | kJ/m2 | ISO 180 |
| Charpy Unnotched Impact Strength (1eU, -20°C) | 54 | kJ/m2 | ISO 180 |
| Charpy Notched Impact Strength (1eA, 23°C) | 13 | kJ/m2 | ISO 179 |
| Charpy Notched Impact Strength (1eA, -20°C) | 10 | kJ/m | ISO 179 |
| Value | Units | Test Method / Conditions | |
| Heat Deflection Temperature - HDT/B (0.45 MPa) | 160 | °C | ISO 75 |
| Vicat Softening Temperature (A120) | 163 | °C | ISO 306 |
| Heat Deflection Temperature - HDT/A (1.8 MPa) | 145 | °C | ISO 75-1,-2 |
| Vicat Softening Temperature (B120) | 136 | °C | ISO 306 |
| Value | Units | Test Method / Conditions | |
| Recommended Processing Parameters | Injection Molding | - | — |
| Barrel Temperatures | 190 to 230 | °C | — |
| Injection Speed | Intermediate | - | — |
| Mold Temperature | 10 to 50 | °C | — |
| Polymer Melt Temperature | 210 to 250 | °C | — |
| Hold Pressure | 30 – 100 % of injection pressure | - | — |
| Value | Units | Test Method / Conditions | |
| Abbreviated Term | PP-H GF30 | - | ISO 1043 |