Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Plastics & Elastomers Processing Methods
Properties
- Color
- Physical Properties
- Mechanical Properties
- Thermal Properties
- Processing Information (Extrusion)
- Processing Information (Injection Molding)
- Additional Information
Value | Units | Test Method / Conditions | |
Density (23°C) | 0.98 | g/cm3 | ISO 1183-1 |
Melt Mass Flow Rate - MFR (230°C/2.16kg) | 0.9 | g/10min | ISO 1133 |
Value | Units | Test Method / Conditions | |
Charpy Notched Impact Strength (23°C) | 4 | kJ/m2 | ISO 179/1eA |
Tensile Stress at Yield (50 mm/min) | 34 | MPa | ISO 527-2 |
Tensile Strain at Yield (50 mm/min) | 7 | % | ISO 527-2/1A |
Flexural Modulus (2 mm/min) | 1900 | MPa | ISO 178 |
Charpy Notched Impact Strength (-20°C) | 1.8 | kJ/m2 | ISO 179/1eA |
Tensile Modulus (1 mm/min) | 1800 | MPa | ISO 527-1,-2 |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature (0.45 MPa) | 110 | °C | ISO 75-1,-2 |
Value | Units | Test Method / Conditions | |
Recommended Processing Parameters | Extrusion | - | — |
Barrel Temperatures | 180 to 220 | °C | — |
Die Temperature | 180 to 220 | °C | — |
Polymer Melt Temperature | 190 to 230 | °C | — |
Value | Units | Test Method / Conditions | |
Recommended Processing Parameters | Injection Molding | - | — |
Barrel Temperatures | 190 to 230 | °C | — |
Hold Pressure | 50 – 100 % of actual injection pressure | - | — |
Mold Temperature | 15 to 50 | °C | — |
Polymer Melt Temperature | 240 to 250 | °C | — |
Injection Speed | Slow or Intermediate | - | — |
Value | Units | Test Method / Conditions | |
Abbreviated Term | PP-H TD10 | - | ISO 1043 |