Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
Applications & Uses
- Plastics & Elastomers Processing Methods
Properties
- Color
- Flame Rating
- Flame Rating
- UL 94 V0
- Physical Properties
- Mechanical Properties
- Thermal Properties
- Flammability
- Processing Information (Extrusion)
- Additional Information
| Value | Units | Test Method / Conditions | |
| Density (23°C) | 1.04 | g/cm3 | ISO 1183 |
| Melt Mass Flow Rate - MFR (230°C/2.16kg) | 1 | g/10 min | ISO 1133 |
| Value | Units | Test Method / Conditions | |
| Tensile Stress at Yield (50 mm/min) | 28 | MPa | ISO 527-2 |
| Charpy Notched Impact Strength (-20°C) | 2 | kJ/m2 | ISO 179/1eA |
| Charpy Notched Impact Strength (23°C) | 3 | kJ/m2 | ISO 179/1eA |
| Tensile Strain at Yield (50 mm/min) | 4 | % | ISO 527-2/1A |
| Charpy Unnotched Impact Strength (23°C) | 25 | kJ/m2 | ISO 179/1eU |
| Tensile Modulus (1 mm/min) | 2600 | MPa | ISO 527 |
| Flexural Modulus (2 mm/min) | 2550 | MPa | ISO 178 |
| Value | Units | Test Method / Conditions | |
| Vicat Softening Temperature (A120) | 152 | °C | ISO 306 |
| Heat Deflection Temperature - HDT/B (0.45 MPa) | 103 | °C | ISO 75-1,-2 |
| Heat Deflection Temperature - HDT/B (1.8 MPa) | 60 | °C | ISO 75-1,-2 |
| Vicat Softening Temperature (B120) | 97 | °C | ISO 306 |
| Value | Units | Test Method / Conditions | |
| Burning Behaviour (d=3.2 mm & 1.6 mm) | V-0 | Class | UL-94 |
| Glow Wire Ignition Temperature - GWIT | 890 | °C | IEC 60695-2-13 |
| Value | Units | Test Method / Conditions | |
| Recommended Processing Parameters | Extrusion | - | — |
| Barrel Temperatures | 180 to 230 | °C | — |
| Polymer Melt Temperature | 200 to max. 240 | °C | — |
| Die Temperature | 190 to 230 | °C | — |
| Value | Units | Test Method / Conditions | |
| Abbreviated Term | PPH FR | - | ISO 1043 |
Regulatory & Compliance
- Certifications & Compliance