Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Color
- Physical Properties
- Mechanical Properties
- Thermal Properties
- Processing Parameters
- Additional Information
Value | Units | Test Method / Conditions | |
Density (23°C) | 1.13 | g/cm3 | ISO 1183 |
Melt Mass Volume Rate - MVR (230°C / 5kg) | 2 | ccm/10 min | ISO 1133 |
Value | Units | Test Method / Conditions | |
Charpy Notched Impact Strength (-30°C) | 7 | kJ/m2 | ISO 179/1eA |
Charpy Notched Impact Strength (23°C) | 10 | kJ/m2 | ISO 179/1eA |
Charpy Impact Strength (-30°C) | 40 | kJ/m2 | ISO 179/1eU |
Tensile Strain at Yield (50 mm/min) | 2.8 | % | ISO 527 |
Flexural Modulus (2 mm/min) | 6100 | MPa | ISO 178 |
Tensile Stress at Break (50 mm/min) | 81 | MPa | ISO 527 |
Tensile Stress at Yield (50 mm/min) | 85 | MPa | ISO 527 |
Tensile Modulus (2 mm/min) | 6200 | MPa | ISO 527-1,-2 |
Tensile Strain at Break (50 mm/min) | 4.5 | % | ISO 527-1,-2 |
Charpy Impact Strength (23°C) | 44 | kJ/m2 | ISO 179/1eU |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature - HDT/A (1.8 MPa) | 140 | °C | ISO 75-1/-2 |
Heat Deflection Temperature - HDT/B (0.45 MPa) | 156 | °C | ISO 75 |
Vicat Softening Temperature (A120) | 161 | °C | ISO 306 |
Vicat Softening Temperature (B120) | 130 | °C | ISO 306 |
Value | Units | Test Method / Conditions | |
Barrel Temperatures | 190 to 250 | °C | — |
Polymer Melt Temperature | 230 to 260 | °C | — |
Injection Speed | Intermediate | - | — |
Mold Temperature | 15 to 60 | °C | — |
Hold Pressure | 50 – 100 % of injection pressure | - | — |
Value | Units | Test Method / Conditions | |
Abbreviated Term | PP-H GF30 | - | ISO 1043 |