Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Color
- Physical Form
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Processing Information (Extrusion)
- Additional Information
Value | Units | Test Method / Conditions | |
Charpy Notched Impact Strength (23°C) | 8 | kJ/m2 | ISO 179/1eA |
Tensile Stress at Yield (50 mm/min) | 33 | MPa | ISO 527-2 |
Charpy Unnotched Impact Strength (23°C) | No Break | - | ISO 179/1eU |
Tensile Strain at Yield (50 mm/min) | 11 | % | ISO 527-2/1A |
Flexural Modulus (2 mm/min) | 1500 | MPa | ISO 178 |
Tensile Modulus (1 mm/min) | 1400 | MPa | ISO 527-1,-2 |
Value | Units | Test Method / Conditions | |
Density (23°C) | 0.9 | g/cm3 | ASTM D792 |
Melt Mass Flow Rate - MFR (230°C/2.16kg) | 0.3 | g/10 min | ISO 1133 |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature - HDT/A (1.8 MPa) | 50 | °C | ISO 75 |
Heat Deflection Temperature - HDT/B (0.45 MPa) | 93 | °C | ISO 75-1,-2 |
Value | Units | Test Method / Conditions | |
Recommended Processing Parameters | Extrusion | - | — |
Barrel Temperatures | 180 to 220 | °C | — |
Polymer Melt Temperature | 200 to 230 (max 240) | °C | — |
Die Temperature | 190 to 220 | °C | — |
Value | Units | Test Method / Conditions | |
Abbreviated Term | PP-H | - | ISO 1043 |