| Value | Units | Test Method / Conditions | |
| Tensile Strain at Yield (50 mm/min) | 9 | % | ISO 527-2/1A |
| Tensile Modulus (1 mm/min) | 900 | MPa | ISO 527 |
| Charpy Notched Impact Strength (23°C) | 40 | kJ/m2 | ISO 179/1eA |
| Charpy Notched Impact Strength (-20°C) | 8 | kJ/m2 | ISO 179/1eA |
| Charpy Impact Strength (23°C) | No Break | kJ/m2 | ISO 179/1eU |
| Tensile Stress at Yield (50 mm/min) | 21 | MPa | ISO 527-1, -2 |
| Charpy Impact Strength (-20°C) | No Break | kJ/m2 | ISO 179/1eU |
| Flexural Modulus (2 mm/min) | 950 | MPa | ISO 178 |
| Value | Units | Test Method / Conditions | |
| Melt Mass Flow Rate - MFR (230°C/2.16kg) | 20 | g/10 min | ISO 1133 |
| Density (23°C) | 0.9 | g/cm3 | ASTM D792 |
| Value | Units | Test Method / Conditions | |
| Heat Deflection Temperature - HDT/A (1.8 MPa) | 50 | °C | ISO 75 |
| Vicat Softening Temperature (A120) | 135 | °C | ISO 306 |
| Vicat Softening Temperature (B120) | 56 | °C | ISO 306 |
| Heat Deflection Temperature - HDT/B (0.45 MPa) | 89 | °C | ISO 75-1,-2 |
| Value | Units | Test Method / Conditions | |
| Recommended Processing Parameters | Injection Molding | - | — |
| Barrel Temperatures | 190 to 230 | °C | — |
| Injection Speed | Intermediate | - | — |
| Hold Pressure | 30 – 100 % of actual injection pressure | - | — |
| Polymer Melt Temperature | 210 to 240 | °C | — |
| Mold Temperature | 10 to 50 | °C | — |
| Value | Units | Test Method / Conditions | |
| Abbreviated Term | PP/PE | - | ISO 1043 |