Value | Units | Test Method / Conditions | |
Charpy Notched Impact Strength (23°C) | 7 | kJ/m2 | ISO 179-1/1eA |
Charpy Notched Impact Strength (-20°C) | 4.5 | kJ/m2 | ISO 179/1eA |
Tensile Stress at Yield (50 mm/min) | 44 | MPa | ISO 527 |
Tensile Strain at Yield (50 mm/min) | 2.7 | % | ISO 527 |
Flexural Modulus (2 mm/min) | 3200 | MPa | ISO 178 |
Tensile Modulus (2 mm/min) | 3300 | MPa | ISO 527-1,-2 |
Charpy Impact Strength (23°C) | 30.5 | kJ/m2 | ISO 179/1eU |
Charpy Impact Strength (-20°C) | 33 | kJ/m2 | ISO 179/1eU |
Value | Units | Test Method / Conditions | |
Density (23°C) | 1.05 | g/cm3 | ISO 1183 |
Melt Mass Flow Rate - MFR (230°C/2.16kg) | 22 | g/10 min | ASTM D1238 |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature - HDT/B (0.45 MPa) | 155 | °C | ISO 75 |
Value | Units | Test Method / Conditions | |
Recommended Processing Parameters | Injection Molding | - | — |
Barrel Temperatures | 190 to 230 | °C | — |
Injection Speed | Intermediate | - | — |
Polymer Melt Temperature | 210 to 240 | °C | — |
Mold Temperature | 10 to 50 | °C | — |
Hold Pressure | 50 – 100 % of actual injection pressure | - | — |
Value | Units | Test Method / Conditions | |
Abbreviated Term | PP/PE TD10 | - | ISO 1043 |