INNOPOL® CS 2-3120 BPLU

Identification & Functionality

Chemical Family

Polyolefins,

Polypropylenes (PP)

Fillers Included

Talc

Polymer Name

Polypropylene Block Copolymer (PP Block Copolymer)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Basic Thermoplastics

Polyolefins

Features & Benefits

Materials Features

UV Stabilized

Applications & Uses

Markets

Agriculture & Feed,

Building & Construction

Applications

Agriculture & Feed — Agricultural Films

Pipes & Hoses

Building & Construction — Building Materials

Pipes & Plumbing

Plastics & Elastomers End Uses

Pipes

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Color

Black

Mechanical Properties

	Value	Units	Test Method / Conditions
Charpy Notched Impact Strength (23°C)	5	kJ/m2	ISO 179-1/1eA
Tensile Stress at Yield (50 mm/min)	28	MPa	ISO 527-2
Charpy Notched Impact Strength (-30°C)	3	kJ/m2	ISO 179/1eA
Tensile Modulus (1 mm/min)	2530	MPa	ISO 527
Tensile Strain at Yield (50 mm/min)	3.5	%	ISO 527
Charpy Impact Strength (-30°C)	25	kJ/m2	ISO 179/1eU
Nominal Tensile Strain at Break	15	%	ISO 527-1,-2
Charpy Impact Strength (23°C)	65	kJ/m2	ISO 179/1eU
Flexural Modulus (2 mm/min)	2740	MPa	ISO 178

Physical Properties

	Value	Units	Test Method / Conditions
Density (23°C)	1.05	g/cm3	ISO 1183
Melt Volume Flow Rate - MVR (230°C/2.16kg)	14	cm3/10 min	ISO 1133
Molding Shrinkage - Across Flow	0.8	%	ASTM D955
Molding Shrinkage - Parallel	1	%	ISO 294-4, 2577
Melt Mass Flow Rate - MFR (230°C/2.16kg)	13	g/10 min	ASTM D1238

Thermal Properties

	Value	Units	Test Method / Conditions
Melting Temperature (DSC)	165	°C	ISO 11357-3
Heat Deflection Temperature - HDT/B (0.45 MPa)	125	°C	ISO 75-2
Vicat Softening Temperature (A120)	-	°C	ISO 306
Vicat Softening Temperature (B120)	-	°C	ISO 306
Heat Deflection Temperature - HDT/A (1.8 MPa)	62	°C	ISO 75-1,-2

Flammability

	Value	Units	Test Method / Conditions
Automotive Materials (thickness d ≥ 1 mm)	+	-	FMVSS 302

Other Properties

	Value	Units	Test Method / Conditions
Ash Content (600°C)	20	%	ISO 3451-1/A

Processing Information (Injection Molding)

	Value	Units	Test Method / Conditions
Recommended Processing Parameters	Injection Molding	-	—
Mold Temperature	20 to 50	°C	—
Injection Speed	Intermediate	-	—
Barrel Temperatures	190 to 250	°C	—
Polymer Melt Temperature	210 to 260	°C	—
Hold Pressure Time	as low as possible – to avoid sink marks	-	—

Additional Information

	Value	Units	Test Method / Conditions
Abbreviated Term	PP/PE TD 20	-	ISO 1043