INNOPOL® CS 2-3120 KAR NU

Identification & Functionality

Chemical Family

Polyolefins,

Polypropylenes (PP)

Fillers Included

Talc

Polymer Name

Polypropylene Block Copolymer (PP Block Copolymer)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Basic Thermoplastics

Polyolefins

Features & Benefits

Materials Features

Good Thermal Stability,

High Stiffness,

High Strength,

Low Shrinkage

Applications & Uses

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Color

Natural

Physical Properties

	Value	Units	Test Method / Conditions
Density (23°C)	1.05	g/cm3	ISO 1183
Melt Mass Flow Rate - MFR (230°C/2.16kg)	18	g/10min	ISO 1133

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress at Yield (50 mm/min)	25	MPa	ISO 527-2
Charpy Notched Impact Strength (-20°C)	2.5	kJ/m2	ISO 179/1eA
Tensile Strain at Yield (50 mm/min)	4	%	ISO 527-2/1A
Charpy Notched Impact Strength (23°C)	4.2	kJ/m2	ISO 179/1eA
Flexural Modulus (2 mm/min)	2200	MPa	ISO 178
Tensile Modulus (1 mm/min)	2300	MPa	ISO 527
Charpy Impact Strength (23°C)	74	kJ/m2	ISO 179/1eU

Thermal Properties

	Value	Units	Test Method / Conditions
Vicat Softening Temperature (A120)	150	°C	ISO 306
Vicat Softening Temperature (B120)	78	°C	ISO 306
Heat Deflection Temperature - HDT/A (1.8 MPa)	118	°C	ISO 75-1,-2
Heat Deflection Temperature - HDT/B (0.45 MPa)	60	°C	ISO 75-1,-2

Processing Information (Injection Molding)

	Value	Units	Test Method / Conditions
Recommended Processing Parameters	Injection Molding	-	—
Injection Speed	Intermediate	-	—
Barrel Temperatures	190 to 250	°C	—
Polymer Melt Temperature	210 to 260	°C	—
Mold Temperature	15 to 50	°C	—
Hold Pressure	50 – 100 % of injection pressure	-	—

Additional Information

	Value	Units	Test Method / Conditions
Abbreviated Term	PP/PE TD 20	-	ISO 1043