Value | Units | Test Method / Conditions | |
Tensile Strain at Yield (50 mm/min) | 5.5 | % | ISO 527-2 |
Tensile Stress at Yield (50 mm/min) | 17 | MPa | ISO 527-2/1A |
Charpy Impact Strength (23°C) | No Break | kJ/m2 | ISO 179/1eU |
Charpy Notched Impact Strength (-20°C) | 11 | kJ/m2 | ISO 179 |
Flexural Modulus (2 mm/min) | 900 | MPa | ISO 178 |
Tensile Modulus (1 mm/min) | 910 | MPa | ISO 527-1,-2 |
Charpy Notched Impact Strength (23°C) | 64.5 | kJ/m2 | ISO 179/1eA |
Value | Units | Test Method / Conditions | |
Melt Mass Flow Rate - MFR (230°C/2.16kg) | 12 | g/10min | ISO 1133 |
Density (23°C) | 0.91 | g/cm3 | ISO 1183-1 |
Value | Units | Test Method / Conditions | |
Recommended Processing Parameters | Injection Molding | - | — |
Injection Speed | Intermediate | - | — |
Hold Pressure | 30 – 100 % of actual injection pressure | - | — |
Mold Temperature | 10 to 50 | °C | — |
Barrel Temperatures | 190 to 240 | °C | — |
Polymer Melt Temperature | 210 to 250 | °C | — |
Value | Units | Test Method / Conditions | |
Abbreviated Term | PP/PE | - | ISO 1043 |