Value | Units | Test Method / Conditions | |
Charpy Unnotched Impact Strength (23°C) | 19 | kJ/m2 | ISO 179/1eU |
Tensile Stress at Yield (50 mm/min) | 25 | MPa | ISO 527-2 |
Charpy Notched Impact Strength (23°C) | 2.7 | kJ/m2 | ISO 179/1eA |
Charpy Unnotched Impact Strength (-20°C) | 10 | kJ/m2 | ISO 179 |
Tensile Strain at Yield (50 mm/min) | 2.2 | % | ISO 527-1,-2 |
Tensile Modulus (1 mm/min) | 3600 | MPa | ISO 527-1,-2 |
Flexural Strength (1 mm/min) | 40 | MPa | ISO 178 |
Flexural Modulus (1 mm/min) | 3700 | MPa | ISO 178 |
Value | Units | Test Method / Conditions | |
Density (23°C) | 1.24 | g/cm3 | ISO 1183 |
Melt Mass Flow Rate - MFR (230°C/2.16kg) | 2 | g/10min | ISO 1133 |
Value | Units | Test Method / Conditions | |
Vicat Softening Temperature (A120) | 150 | °C | ISO 306 |
Vicat Softening Temperature (B120) | 84 | °C | ISO 306 |
Heat Deflection Temperature - HDT/A (1.8 MPa) | 61 | °C | ISO 75-1,-2 |
Heat Deflection Temperature - HDT/B (0.45 MPa) | 114 | °C | ISO 75-1,-2 |
Value | Units | Test Method / Conditions | |
Barrel Temperatures | 190 to 230 | °C | — |
Polymer Melt Temperature | 230 to 250 | °C | — |
Mold Temperature | 10 to 50 | °C | — |
Injection Speed | Slow or Intermediate | - | — |
Hold Pressure | 50 – 100 % of actual injection pressure | - | — |
Value | Units | Test Method / Conditions | |
Abbreviated Term | PP/PE TD40 | - | ISO 1043 |