Properties
- Color
- Physical Form
- Physical Properties
- Mechanical Properties
- Thermal Properties
- Processing Information (Extrusion)
Value | Units | Test Method / Conditions | |
Density (23°C) | 1.04 | g/cm3 | ISO 1183 |
Melt Mass Flow Rate - MFR (230°C/5kg) | 0.8 | g/10 min | ISO 1133 |
Value | Units | Test Method / Conditions | |
Tensile Stress at Yield (50 mm/min) | 24 | MPa | ISO 527-2 |
Charpy Notched Impact Strength (-20°C) | 4 | kJ/m2 | ISO 179/1eA |
Charpy Notched Impact Strength (23°C) | 20 | kJ/m2 | ISO 179/1eA |
Tensile Strain at Yield (50 mm/min) | 6 | % | ISO 527-2/1A |
Tensile Modulus (1 mm/min) | 1700 | MPa | ISO 527 |
Flexural Modulus (2 mm/min) | 1800 | MPa | ISO 178 |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature - HDT/B (0.45 MPa) | 102 | °C | ISO 75-1,-2 |
Value | Units | Test Method / Conditions | |
Recommended Processing Parameters | Extrusion | - | — |
Barrel Temperatures | 180 to 220 | °C | — |
Polymer Melt Temperature | 200 to 230 | °C | — |
Die Temperature | 190 to 220 | °C | — |