Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Color
- Physical Form
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Processing Information (Extrusion)
- Processing Information (Injection Molding)
- Additional Information
| Value | Units | Test Method / Conditions | |
| Charpy Notched Impact Strength (-20°C) | 5 | kJ/m2 | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | - | ISO 179/1eU |
| Charpy Notched Impact Strength (23°C) | 60 | kJ/m2 | ISO 179/1eA |
| Tensile Modulus (1A/1) | 1450 | MPa | ISO 527-1,-2 |
| Tensile Stress at Yield (1A/50) | 30 | MPa | ISO 527-1,-2 |
| Tensile Strain at Yield (1A/50) | 8 | % | ISO 527-1,-2 |
| Tensile Stress at Break (1A/50) | 20 | MPa | ISO 527-1,-2 |
| Tensile Strain at Break (1A/50) | 65 | % | ISO 527-1,-2 |
| Flexural Modulus (1A/2) | 1500 | MPa | ISO 178 |
| Flexural Strength (1A/2) | 36 | MPa | ISO 178 |
| Value | Units | Test Method / Conditions | |
| Density (23°C) | 0.9 | g/cm3 | ASTM D792 |
| Melt Mass Flow Rate - MFR (230°C/2.16kg) | 0.3 | g/10 min | ISO 1133 |
| Value | Units | Test Method / Conditions | |
| Heat Deflection Temperature - HDT/A (1.8 MPa) | 48 | °C | ISO 75-1,-2 |
| Vicat Softening Temperature (A120) | 158 | °C | ISO 306 |
| Vicat Softening Temperature (B120) | 92 | °C | ISO 306 |
| Heat Deflection Temperature - HDT/B (0.45 MPa) | 92 | °C | ISO 75-1,-2 |
| Oxidation Induction Time - OTI (210°C) | ≥ 20 | min. | ISO 11357-6 |
| Value | Units | Test Method / Conditions | |
| Recommended Processing Parameters | Extrusion | - | — |
| Barrel Temperatures | 180 to 220 | °C | — |
| Polymer Melt Temperature | 200 to 230 | °C | — |
| Die Temperature | 190 to 220 | °C | — |
| Value | Units | Test Method / Conditions | |
| Recommended Processing Parameters | Injection Molding | - | — |
| Hold Pressure | 50 – 100 % of actual injection pressure | - | — |
| Barrel Temperatures | 190 to 240 | °C | — |
| Mold Temperature | 15 to 50 | °C | — |
| Injection Speed | Slow to Intermediate | - | — |
| Polymer Melt Temperature | 240 to 250 | °C | — |
| Value | Units | Test Method / Conditions | |
| Abbreviated Term | PP/PE | - | ISO 1043 |