Value | Units | Test Method / Conditions | |
Melt Mass Flow Rate - MFR (230°C/2.16 kg) | 0.8 | g/10 min | ASTM D1238 |
Density (23°C) | 1.05 | g/cm3 | ISO 1183 |
Molding Shrinkage - Normal | 1.01 | % | ISO 294-4 |
Molding Shrinkage - Parallel | 1.65 | % | ISO 294-4 |
Value | Units | Test Method / Conditions | |
Charpy Notched Impact Strength (-20°C) | 4 | kJ/m2 | ISO 179/1eA |
Tensile Stress at Yield (50 mm/min) | 23 | MPa | ISO 527-2 |
Charpy Notched Impact Strength (23°C) | 20 | kJ/m2 | ISO 179/1eA |
Tensile Strain at Yield (50 mm/min) | 5 | % | ISO 527-2/1A |
Tensile Modulus (1 mm/min) | 2000 | MPa | ISO 527 |
Flexural Modulus (2 mm/min) | 2100 | MPa | ISO 178 |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature - HDT/B (0.45 MPa) | 104 | °C | ISO 75-1,-2 |
Value | Units | Test Method / Conditions | |
Recommended Processing Parameters | Extrusion | - | - |
Barrel Temperatures | 180 to 220 | °C | - |
Polymer Melt Temperature | 200 to 230 | °C | - |
Die Temperature | 190 to 220 | °C | - |
Value | Units | Test Method / Conditions | |
Abbreviated Term | PP/PE TD20 | - | ISO 1043 |