INNOPOL® CS 2-8660 FR

Identification & Functionality

Additives Included

Flame Retardant

Chemical Family

Polyolefins,

Polypropylenes (PP)

Polymer Name

Polypropylene Block Copolymer (PP Block Copolymer)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Basic Thermoplastics

Polyolefins

Features & Benefits

Materials Features

Elastomer Modified,

Flame Retardant

Applications & Uses

Plastics & Elastomers Processing Methods

Extrusion,

Injection Molding

Properties

Color

Natural

Flame Rating

UL 94 V0

Flame Rating

UL 94 V0

Mechanical Properties

	Value	Units	Test Method / Conditions
Charpy Notched Impact Strength (23°C)	45	kJ/m2	ISO 179-1/1eA
Charpy Notched Impact Strength (-20°C)	4.5	kJ/m2	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	No Break	-	ISO 179/1eU
Tensile Strain at Break (50 mm/min)	70	%	ISO 527
Flexural Modulus (2 mm/min)	1800	MPa	ISO 178
Charpy Unnotched Impact Strength (-20°C)	22	kJ/m2	ISO 179
Tensile Strain at Yield (50 mm/min)	2.2	%	ISO 527-1,-2
Tensile Modulus (2 mm/min)	1700	MPa	ISO 527-1,-2
Tensile Stress at Yield (50 mm/min)	13.5	MPa	ISO 527-1,-2
Tensile Stress at Break (50 mm/min)	11.5	MPa	ISO 527-1,-2
Flexural Strength (2 mm/min)	22	MPa	ISO 178

Physical Properties

	Value	Units	Test Method / Conditions
Density (23°C)	1.42	g/cm3	ISO 1183
Melt Volume Flow Rate - MVR (230 °C/2.16kg)	0.5	ccm/10 min	ISO 1133

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (0.45 MPa)	110	°C	ISO 75-1,-2

Flammability

	Value	Units	Test Method / Conditions
Burning Behaviour (3.2mm)	V0	Class	UL-94

Processing Information (Extrusion)

	Value	Units	Test Method / Conditions
Recommended Processing Parameters	Extrusion	-	—
Barrel Temperatures	180 to 220	°C	—
Die Temperature	190 to 220	°C	—
Polymer Melt Temperature	190 to 220	°C	—

Additional Information

	Value	Units	Test Method / Conditions
Abbreviated Term	PP-B FR	-	ISO 1043

Regulatory & Compliance

Certifications & Compliance

UL 94