INNOPOL® CS 2-8940 BA42 GU

Identification & Functionality

Chemical Family

Polyolefins,

Polypropylenes (PP)

Fillers Included

Barium Sulfate

Polymer Name

Polypropylene Block Copolymer (PP Block Copolymer)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Basic Thermoplastics

Polyolefins

Features & Benefits

Materials Features

Good Thermal Stability,

High Stiffness,

UV Stabilized

Applications & Uses

Plastics & Elastomers Processing Methods

Extrusion,

Injection Molding

Properties

Color

Grey

Physical Properties

	Value	Units	Test Method / Conditions
Density (23°C)	1.4	g/cm3	ASTM D1505
Melt Volume Flow Rate - MVR (230°C/2.16kg)	0.9	cm/10 min	ISO 1133

Mechanical Properties

	Value	Units	Test Method / Conditions
Charpy Notched Impact Strength (-20°C)	4.5	kJ/m2	ISO 179/1eA
Charpy Notched Impact Strength (23°C)	20	kJ/m2	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	No Break	-	ISO 179/1eU
Tensile Strain at Yield (50 mm/min)	7	%	ISO 527-2/1A
Tensile Stress at Yield (50 mm/min)	19	MPa	ISO 527-1, -2
Tensile Stress at Break (50 mm/min)	23	MPa	ISO 527
Flexural Modulus (2 mm/min)	1650	MPa	ISO 178
Tensile Modulus (1 mm/min)	1650	MPa	ISO 527-1,-2
Tensile Strain at Break (50 mm/min)	430	%	ISO 527-1,-2
Charpy Unnotched Impact Strength (-20°C)	65	kJ/m2	ISO 179/1eU

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature - HDT/A (1.8 MPa)	46	°C	ISO 75-1/-2
Heat Deflection Temperature - HDT/B (0.45 MPa)	80	°C	ISO 75-1,-2

Processing Information (Extrusion)

	Value	Units	Test Method / Conditions
Recommended Processing Parameters	Extrusion	-	-
Barrel Temperatures	180 to 220	°C	-
Die Temperature	190 to 220	°C	-
Polymer Melt Temperature	190 to 230	°C	-

Processing Information (Injection Molding)

	Value	Units	Test Method / Conditions
Recommended Processing Parameters	Injection Molding	-	-
Polymer Melt Temperature	230 to 250	°C	-
Hold Pressure	50 – 100 % of actual injection pressure	-	-
Barrel Temperatures	190 to 240	°C	-
Mold Temperature	15 to 50	°C	-
Injection Speed	Slow to Intermediate	-	-

Additional Information

	Value	Units	Test Method / Conditions
Abbreviated Term	PP/PE BAS42	-	ISO 1043