INNOPOL® CS 2-8960 BA60

Identification & Functionality

Chemical Family

Polyolefins,

Polypropylenes (PP)

Fillers Included

Barium Sulfate

Polymer Name

Polypropylene Block Copolymer (PP Block Copolymer)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Basic Thermoplastics

Polyolefins

Features & Benefits

Materials Features

Good Stiffness

Applications & Uses

Plastics & Elastomers Processing Methods

Extrusion,

Injection Molding

Properties

Color

Natural

Mechanical Properties

	Value	Units	Test Method / Conditions
Charpy Notched Impact Strength (-20°C)	3	kJ/m2	ISO 179/1eA
Charpy Notched Impact Strength (23°C)	20	kJ/m2	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	No Break	-	ISO 179/1eU
Tensile Strain at Yield (50 mm/min)	4	%	ISO 527-2/1A
Tensile Stress at Yield (50 mm/min)	16	MPa	ISO 527-1, -2
Tensile Stress at Break (50 mm/min)	17	MPa	ISO 527
Tensile Modulus (1 mm/min)	1900	MPa	ISO 527
Flexural Modulus (2 mm/min)	2050	MPa	ISO 178
Charpy Unnotched Impact Strength (-20°C)	35	kJ/m2	ISO 179/1eU
Tensile Strain at Break (50 mm/min)	145	%	ISO 527-1,-2

Physical Properties

	Value	Units	Test Method / Conditions
Density (23°C)	1.75	g/cm3	ISO 1183
Melt Volume Flow Rate - MVR (230°C/2.16kg)	0.9	cm/10 min	ISO 1133

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature - HDT/A (1.8 MPa)	46	°C	ISO 75-1/-2
Heat Deflection Temperature - HDT/B (0.45 MPa)	80	°C	ISO 75-1,-2

Processing Information (Extrusion)

	Value	Units	Test Method / Conditions
Recommended Processing Parameters	Extrusion	-	—
Barrel Temperatures	180 to 220	°C	—
Polymer Melt Temperature	200 to 230	°C	—
Die Temperature	190 to 220	°C	—

Additional Information

	Value	Units	Test Method / Conditions
Abbreviated Term	PP/PE BAS60	-	ISO 1043