INNOPOL® CS 2-9000 BU/3

Identification & Functionality

Additives Included

Flame Retardant

Chemical Family

Polyolefins,

Polypropylenes (PP)

Polymer Name

Polypropylene Block Copolymer (PP Block Copolymer)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Basic Thermoplastics

Polyolefins

Features & Benefits

Materials Features

Flame Retardant,

Good Stiffness,

UV Stabilized

Applications & Uses

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Color

Black

Flame Rating

UL 94 HB

Flame Rating

UL 94 HB

Mechanical Properties

	Value	Units	Test Method / Conditions
Charpy Notched Impact Strength (23°C)	7	kJ/m2	ISO 179-1/1eA
Tensile Stress at Yield (50 mm/min)	26	MPa	ISO 527-2
Charpy Notched Impact Strength (-30°C)	3	kJ/m2	ISO 179/1eA
Tensile Strain at Yield (50 mm/min)	8	%	ISO 527-1,-2
Tensile Modulus (1 mm/min)	1300	MPa	ISO 527-1,-2

Physical Properties

	Value	Units	Test Method / Conditions
Molding Shrinkage - Normal	1.1	%	ISO 294-4, 2577
Density (23°C)	0.91	g/cm3	ISO 1183-1
Molding Shrinkage - Parallel	1.2	%	ISO 1183
Melt Mass Flow Rate - MFR (230°C/2.16kg)	50	g/10 min	ASTM D1238

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature - HDT/A (1.8 MPa)	52	°C	ISO 75-1,-2
Heat Deflection Temperature - HDT/B (0.45 MPa)	105	°C	ISO 75-1,-2

Flammability

	Value	Units	Test Method / Conditions
Automotive Materials (thickness d ≥ 1 mm)	+	-	FMVSS 302
Burning Behaviour (d=3.2 mm)	HB	Class	UL-94

Processing Information (Injection Molding)

	Value	Units	Test Method / Conditions
Recommended Processing Parameters	Injection Molding	-	—
Barrel Temperatures	190 to 230	°C	—
Injection Speed	Intermediate	-	—
Hold Pressure	30 – 100 % of actual injection pressure	-	—
Polymer Melt Temperature	210 to 240	°C	—
Mold Temperature	10 to 50	°C	—

Additional Information

	Value	Units	Test Method / Conditions
Abbreviated Term	PP/PE	-	ISO 1043

Regulatory & Compliance

Certifications & Compliance

UL 94