Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Color
- Physical Form
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Flammability
- Processing Information (Injection Molding)
- Additional Information
| Value | Units | Test Method / Conditions | |
| Charpy Notched Impact Strength (-30°C) | 4 | kJ/m2 | ISO 179-1/1eA |
| Tensile Stress at Yield (50 mm/min) | 28 | MPa | ISO 527-2 |
| Tensile Strain at Yield (50 mm/min) | 5 | % | ISO 527-2/1A |
| Charpy Impact Strength (23°C) | No Break | kJ/m2 | ISO 179/1eU |
| Flexural Modulus (2 mm/min) | 1500 | MPa | ISO 178 |
| Tensile Modulus (1 mm/min) | 1480 | MPa | ISO 527-1,-2 |
| Nominal Tensile Strain at Break | 24 | % | ISO 527-1,-2 |
| Charpy Notched Impact Strength (23°C) | PB (80) | kJ/m2 | ISO 179/1eA |
| Value | Units | Test Method / Conditions | |
| Density (23°C) | 0.9 | g/cm3 | ASTM D792 |
| Molding Shrinkage - Parallel | 1.4 | % | ISO 294-4, 2577 |
| Molding Shrinkage - Normal | 2.2 | % | ISO 294 |
| Melt Mass Flow Rate - MFR (230°C/2.16kg) | 48 | g/10 min | ISO 1133 |
| Melt Volume Flow Rate - MVR (230°C/2.16kg) | 62 | ml/10 min | ISO 1133 |
| Value | Units | Test Method / Conditions | |
| Melting Temperature (DSC) | 163 | °C | ISO 3146 |
| Heat Deflection Temperature - HDT/A (1.8 MPa) | 57 | °C | ISO 75-1/-2 |
| Vicat Softening Temperature (B120) | 78 | °C | ISO 306 |
| Vicat Softening Temperature (A120) | 148 | °C | ISO 306 |
| Heat Deflection Temperature - HDT/B (0.45 MPa) | 108 | °C | ISO 75-1,-2 |
| Value | Units | Test Method / Conditions | |
| Automotive Materials (thickness d ≥ 1 mm) | + | - | FMVSS 302 |
| Value | Units | Test Method / Conditions | |
| Recommended Processing Parameters | Injection Molding | - | - |
| Injection Speed | Intermediate | - | - |
| Mold Temperature | 10 to 50 | °C | - |
| Hold Pressure | 50 – 100 % of actual injection pressure | - | - |
| Barrel Temperatures | 190 to 250 | °C | - |
| Polymer Melt Temperature | 210 to 260 | °C | - |
| Value | Units | Test Method / Conditions | |
| Abbreviated Term | PP / PE | - | ISO 1043 |