INNOPOL® CS 2-9120 BPL

Identification & Functionality

Chemical Family

Polyolefins,

Polypropylenes (PP)

Fillers Included

Talc

Polymer Name

Polypropylene Block Copolymer (PP Block Copolymer)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Basic Thermoplastics

Polyolefins

Features & Benefits

Materials Features

High Stiffness,

High Strength

Applications & Uses

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Color

Black

Mechanical Properties

	Value	Units	Test Method / Conditions
Charpy Notched Impact Strength (23°C)	4	kJ/m2	ISO 179/1eA
Charpy Notched Impact Strength (-20°C)	2.5	kJ/m2	ISO 179/1eA
Tensile Stress at Yield (50 mm/min)	22	MPa	ISO 527-1, -2
Tensile Strain at Yield (50 mm/min)	2.5	%	ISO 527-2/1A
Flexural Modulus (2 mm/min)	2300	MPa	ISO 178
Tensile Modulus (1 mm/min)	2300	MPa	ISO 527

Physical Properties

	Value	Units	Test Method / Conditions
Density (23°C)	1.04	g/cm3	ISO 1183
Melt Mass Flow Rate - MFR (230°C/2.16kg)	25	g/10 min	ASTM D1238

Processing Information (Injection Molding)

	Value	Units	Test Method / Conditions
Recommended Processing Parameters	Injection Molding	-	-
Injection Speed	Intermediate	-	-
Hold Pressure	30 – 100 % of actual injection pressure	-	-
Mold Temperature	10 to 50	°C	-
Barrel Temperatures	190 to 240	°C	-
Polymer Melt Temperature	210 to 250	°C	-

Additional Information

	Value	Units	Test Method / Conditions
Abbreviated Term	PP/PE TD 20	-	ISO 1043