Value | Units | Test Method / Conditions | |
Tensile Stress at Yield (50 mm/min) | 30 | MPa | ISO 527-2 |
Charpy Notched Impact Strength (-20°C) | 2 | kJ/m2 | ISO 179/1eA |
Charpy Notched Impact Strength (23°C) | 3.5 | kJ/m2 | ISO 179/1eA |
Tensile Strain at Yield (50 mm/min) | 5 | % | ISO 527-2/1A |
Flexural Modulus (2 mm/min) | 2800 | MPa | ISO 178 |
Tensile Modulus (1 mm/min) | 2600 | MPa | ISO 527 |
Value | Units | Test Method / Conditions | |
Melt Mass Flow Rate - MFR (230°C/2.16kg) | 10 | g/10min | ISO 1133 |
Density (23°C) | ["1.05"] | g/cm3 | ISO 1183 |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature - HDT/B (0.45 MPa) | 125 | °C | ISO 75-2 |
Value | Units | Test Method / Conditions | |
Polymer Melt Temperature | 230 to 250 | °C | — |
Mold Temperature | 15 to 50 | °C | — |
Injection Speed | Intermediate | - | — |
Hold Pressure | 50 – 100 % of maximum injection | - | — |
Barrel Temperatures | 210 to 240 | °C | — |
Value | Units | Test Method / Conditions | |
Abbreviated Term | PP TD20 | - | ISO 1043 |