Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Applications
- Plastics & Elastomers Processing Methods
Properties
- Color
- Physical Form
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Processing Information (Extrusion)
- Additional Information
| Value | Units | Test Method / Conditions | |
| Charpy Notched Impact Strength (23°C) | 15 | kJ/m2 | ISO 179/1eA |
| Charpy Notched Impact Strength (-20°C) | 8 | kJ/m2 | ISO 179/1eA |
| Tensile Modulus (1 mm/min) | 2850 | MPa | ISO 527-1,-2 |
| Tensile Stress at Yield (1A/50) | 50 | MPa | ISO 527-1,-2 |
| Tensile Strain at Yield (1A/50) | 5 | % | ISO 527-1,-2 |
| Tensile Stress at Break (1A/50) | 50 | MPa | ISO 527-1,-2 |
| Tensile Strain at Break (1A/50) | 7 | % | ISO 527-1,-2 |
| Value | Units | Test Method / Conditions | |
| Density (23°C) | 0.99 | g/cm3 | ISO 1183-1 |
| Melt Mass Flow Rate - MFR (230°C/2.16kg) | 0.5 | g/10 min | ISO 1133 |
| Value | Units | Test Method / Conditions | |
| Heat Deflection Temperature - HDT/A (1.8 MPa) | 80 | °C | ISO 75-1/-2 |
| Vicat Softening Temperature (A120) | 140 | °C | ISO 306 |
| Vicat Softening Temperature (B120) | 100 | °C | ISO 306 |
| Heat Deflection Temperature - HDT/B (0.45 MPa) | 130 | °C | ISO 75-1,-2 |
| Value | Units | Test Method / Conditions | |
| Recommended Processing Parameters | Extrusion | - | — |
| Barrel Temperatures | 180 to 220 | °C | — |
| Die Temperature | 190 to 220 | °C | — |
| Polymer Melt Temperature | 200 to 220 | °C | — |
| Value | Units | Test Method / Conditions | |
| Abbreviated Term | PP-R GF15 | - | ISO 1043 |