Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Color
- Physical Properties
- Mechanical Properties
- Thermal Properties
- Processing Information (Extrusion)
- Additional Information
| Value | Units | Test Method / Conditions | |
| Density (23°C) | 1.13 | g/cm3 | ISO 1183 |
| Melt Mass Flow Rate - MFR (230°C/2.16kg) | 0.4 | g/10 min | ISO 1133 |
| Value | Units | Test Method / Conditions | |
| Charpy Notched Impact Strength (-20°C) | 10 | kJ/m2 | ISO 179 |
| Tensile Modulus (1 mm/min) | 4800 | MPa | ISO 527 |
| Tensile Strain at Yield (1A/50) | 5 | % | ISO 527-1,-2 |
| Tensile Stress at Yield (1A/50) | 65 | MPa | ISO 527-1,-2 |
| Tensile Stress at Break (1A/50) | 65 | MPa | ISO 527-1,-2 |
| Tensile Strain at Break (1A/50) | 6 | % | ISO 527-1,-2 |
| Charpy Notched Impact Strength (23°C) | 18.5 | kJ/m2 | ISO 180/1A |
| Charpy Impact Strength (23°C) | 58 | kJ/m2 | ISO 179/1eU |
| Charpy Impact Strength (-20°C) | 50 | kJ/m2 | ISO 179/1eU |
| Flexural Strength (1A/2) | 91 | MPa | ISO 178 |
| Flexural Modulus (1A/2) | 4600 | MPa | ISO 178 |
| Value | Units | Test Method / Conditions | |
| Vicat Softening Temperature (A120) | 140 | °C | ISO 306 |
| Vicat Softening Temperature (B120) | 106 | °C | ISO 306 |
| Heat Deflection Temperature - HDT/A (1.8 MPa) | 110 | °C | ISO 75-1,-2 |
| Heat Deflection Temperature - HDT/B (0.45 MPa) | 142 | °C | ISO 75-1,-2 |
| Value | Units | Test Method / Conditions | |
| Recommended Processing Parameters | Extrusion | - | — |
| Barrel Temperatures | 180 to 220 | °C | — |
| Die Temperature | 190 to 220 | °C | — |
| Polymer Melt Temperature | 200 to 220 | °C | — |
| Value | Units | Test Method / Conditions | |
| Abbreviated Term | PP-R GF30 | - | ISO 1043 |