Properties
- Typical Properties
| Value | Units | Test Method / Conditions | |
| Dart Drop Impact (2.0 mil (51 µm)) | 88 | g | ASTM D1709A |
| Density | 0.922 | g/cm³ | ASTM D 792 |
| Elmendorf Tear Strength (2.0 mil (51 µm)) (MD) | 440 | g | ASTM D1922 |
| Elmendorf Tear Strength (2.0 mil (51 µm)) (TD) | 480 | g | ASTM D1922 |
| Film Puncture Resistance (2.00 mil (51) µm)) | 51 (4.22) | ft-lb/in³ (J/m³) | - |
| Film Thickness - Tested | 2.0 (51) | mil (µm) | - |
| Film Toughness (2.0 mil (51 µm)) (MD) | 2680 (221) | ft-lb/in³ (J/m³) | ASTM D 882 |
| Film Toughness (2.0 mil (51 µm)) (TD) | 2210 (183) | ft-lb/in³ (J/m³) | ASTM D 882 |
| Gloss (2.00 mil (50.8) µm)) | 76 | - | ASTM D2457 |
| Haze (2.00 mil (50.8) µm)) | 6.7 | % | ASTM D1003 |
| Melt Index (190°C/2.16 kg) | 1.9 | g/10 min | ASTM D1238 |
| Melt Temperature | 422 (217) | °F (°C) | - |
| Melting Temperature (DSC) | 232 (111) | °F (°C) | - |
| Tensile Elongation at Break (2.0 mil (51 µm)) (MD) | 650 | % | ASTM D 882 |
| Tensile Elongation at Break (2.0 mil (51 µm)) (TD) | 730 | % | ASTM D 882 |
| Tensile Strength at Break (2.0 mil (51 µm)) (MD) | 3700 (25.5)V | psi (Mpa) | ASTM D 882 |
| Tensile Strength at Break (2.0 mil (51 µm)) (TD) | 2840 (19.6) | psi (Mpa) | ASTM D 882 |
| Tensile Strength at Yield (2.0 mil (51 µm)) (MD) | 1760 (12.2) | psi (Mpa) | ASTM D 882 |
| Tensile Strength at Yield (2.0 mil (51 µm)) (TD) | 3700 (25.5) | psi (Mpa) | ASTM D 882 |
| Vicat Softening Temperature | 198 (92.2) | °F (°C) | ASTM D1525 |