Grade PE2NT74-15 is intended for further processing by extrusion blow molding method into domestic and industrial-use articles with a capacity of 3-20 liters such as flasks, water bottles, bottles for household chemistry and HIGH DENSITY POLYETHYLENE cosmetics.
Properties
- Typical Properties
| Value | Units | Test Method / Conditions | |
| Density at 23°C | 946 - 953 | kg/m3 | — |
| Density at 20°C | 949 - 955 | kg/m3 | — |
| Melt Flow Index at 190 °С and Load of 49 N (5kgf) | 1.5 - 2.0 | g/10 min | — |
| Tensile Yield Strength | min. 26 | MPa | — |
| Rupture Strength | min. 30 | MPa | — |
| Elongation at Break | min. 750 | % | — |
| Cracking Resistance | min. 60 | hours | — |
Packaging & Availability
- Packing
Product is packed in polyethylene bags (one bag net weight 25.00±0.25kg) and stacked on flat pallets with shrink film. Maximum gross weight of a bundle is 2 tons.
- Transportation
By all modes of transport.
Storage & Handling
- Storage
Polyethylene shall be stored in enclosed dry space preventing from direct sunlight on shelves or pallets at least 5 cm from the floor and at least 1 m from heaters, at temperature max 30°C, relative humidity max 80 %. Prior to processing bags with polymer shall be kept in production area for at least 12 hrs.