Glass fiber and mineral reinforced polyamide 6 compound. The material features high mechanical strength, dimensional stability, narrow range of shrinkage, low warp. The material has chemical resistance to hydrocarbons, mineral oils, concentrated and weak alkalis, weak acids.
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Application
For injection molding of different parts in automotive, machine-building, electrical and furniture industries, production of household and other articles
- Processing
Melt temperature 230 ÷ 260 ºС. To avoid degradation it is recommended to limit injection molding temperature to 290 ºС.
Injection pressure 80 ÷ 130 MPa, recommended 90 MPa.
Mold temperature 60 ÷ 90 ºС. A higher mold temperature leads to higher shrinkage.
Properties
- Chemical Resistance
- Typical Properties
| Value | Units | Test Method / Conditions | |
| Melt Flow Rate (270 °C, 2.16 kg load) | 16 - 20 | g/10 min | ISO 1133 |
| Molding Shrinkage (60×60×2 mm) | 0.5 - 0.8 | % | ISO 294-4 |
| Tensile Strength (5 mm/min) | 105 | MPa | ISO 527 |
| Elongation at Break (5 mm/min) | 3 | % | ISO 527 |
| Tensile Modulus (1 mm/min) | 6800 | MPa | ISO 527 |
| Flexural Stress (2 mm/min) | 190 | MPa | ISO 178 |
| Flexural Modulus (2 mm/min) | 7300 | MPa | ISO 178 |
| Charpy Impact Strength (+23°C) | 40 | kJ/m2 | ISO 179/1eU |
| Charpy Notched Impact Strength (+23°C) | 7 | kJ/m2 | ISO 179/1eA |
| Melting Point (10 °C/ min) | 217 | °C | ISO 3146 |
| Temperature of Deflection under load 0.45 MPa | 180 - 190 | °C | ISO 75-1/-2 |
| Temperature of Deflection under load 1.80 MPa | 170 - 180 | °C | ISO 75-1/-2 |
| Volume Resistivity | 10^12 | Ohm×m | IEC 60093 |
| Surface Resistivity | 10^12 | Ohm | IEC 60093 |
| Water Absorption,24h/23ºC | 1.3 | % | Sim. to ISO 62 |
| Water Absorption, 30 min at boiling | 1.6 | % | Sim. to ISO 62 |
| Moisture Absorption from Air | 1.9 | % | Sim. to ISO 62 |
| Density | 1.35 | g/cm3 | ISO 1183 |
Regulatory & Compliance
- Recycling
Clean milled post production wastes could be recycled after mixing with fresh plastics. The amount of milled plastic added to natural plastic is controlled depending on final product quality requirements, it may reach up to 50 %. Final product properties depend rather more on quality of recycled or milled polyamide then on its share. Attention shall be paid not to use milled scraps having more than 0.2 % water.
Technical Details & Test Data
- Preprocessing
Processing moisture content < 0.2 %.
If drying becomes necessary:
- drying in dehumidified dryer, drying temperature 80ºС,
- drying time is dependent on moisture level.
Packaging & Availability
- Packaging Type
- Colour
The material is available in pigmented version.
- Packaging
- PET/ALU/PE bags with/without a degassing valve. The bags are stacked on a pallet with the following stretch-foiling. Bag weight: 25 kg net. Pallet weight: 1000 kg. Quantity to be loaded in a truck (82m3 ) and 40’’ marine container: 20000 kg net (20 pallets).
- Polyethylene bags with a valve. The valve is sealed with scotch film. The bags are stacked on a pallet with the following stretch-foiling. Bag weight: 30 kg net. Pallet weight: 960 kg / Bag weight: 25 kg net. Pallet weight: 1000 kg. Quantity to be loaded in a truck (82m3 ) and 40’’ marine container: 20160 kg net (21 pallets) / 20000 kg net (20 pallets).