External lubricated, easy flowing injection molding grade for fast processing based on virgin PA6.
Applications & Uses
- Applications
- Plastics & Elastomers Processing Methods
- Application
Used for injection molding of different parts in automotive, mechanical engineering, instrumentmaking, where fast processing is required, including production of thin-walled parts.
- Processing
Melt temperature 230 ÷ 260 ºС. To avoid degradation it is recommended to limit injection molding temperature to 290 ºС.
Injection pressure 80 ÷ 130 MPa, recommended 80 MPa.
Mold temperature 50 ÷ 90 ºС. A higher mold temperature leads to higher shrinkage.
Properties
- Typical Properties
| Value | Units | Test Method / Conditions | |
| Melt Flow Rate (230 °C, 2.16 kg load) | 17 - 21 | g/10 min | ISO 1133 |
| Melt Flow Rate (270 °C, 2.16 kg load) | 55 - 65 | g/10 min | ISO 1133 |
| Molding Shrinkage (60×60×2 mm) | 1.2 - 2.0 | % | ISO 294-4 |
| Tensile Strength (20 mm/min) | 73 | MPa | ISO 527 |
| Elongation at Break (20 mm/min) | 95 | % | ISO 527 |
| Tensile Modulus (1 mm/min) | 2600 | MPa | ISO 527 |
| Flexural Stress (2 mm/min) | 75 | MPa | ISO 178 |
| Flexural Modulus (2 mm/min) | 2200 | MPa | ISO 178 |
| Charpy Notched Impact Strength (+23°C) | 9 | kJ/m2 | ISO 179/1eA |
| Melting Point (10 °C/ min) | 217 | °C | ISO 3146 |
| Temperature of Deflection under load 0.45 MPa | 120 - 130 | °C | ISO 75-1/-2 |
| Temperature of Deflection under load 1.80 MPa | 45 - 50 | °C | ISO 75-1/-2 |
| Volume Resistivity | 10^13 | Ohm×m | IEC 60093 |
| Surface Resistivity | 10^13 | Ohm | IEC 60093 |
| Water Absorption,24h/23ºC | 2.3 | % | Sim. to ISO 62 |
| Water Absorption, 30 min at boiling | 2.5 | % | Sim. to ISO 62 |
| Moisture Absorption from Air | 2.5 | % | Sim. to ISO 62 |
| Density | 1.13 | g/cm3 | ISO 1183 |
Regulatory & Compliance
- Recycling
Clean milled post production wastes could be recycled after mixing with fresh plastics. The amount of milled plastic added to natural plastic is controlled depending on final product quality requirements, it may reach up to 50 %. Final product properties depend rather more on quality of recycled or milled polyamide then on its share. Attention shall be paid not to use milled scraps having more than 0.2 % water.
Technical Details & Test Data
- Preprocessing
Processing moisture content < 0.2 %.
If drying becomes necessary:
- drying in dehumidified dryer, drying temperature 80ºС,
- drying time is dependent on moisture level.
Packaging & Availability
- Packaging Type
- Colour
By customer’s request it can be manufactured in pigmented version.
- Packaging
- PET/ALU/PE bags with/without a degassing valve. The bags are stacked on a pallet with the following stretch-foiling. Bag weight: 25 kg net. Pallet weight: 1000 kg. Quantity to be loaded in a truck (82m3 ) and 40’’ marine container: 20000 kg net (20 pallets).
- Polyethylene bags with a valve. The valve is sealed with scotch film. The bags are stacked on a pallet with the following stretch-foiling. Bag weight: 30 kg net. Pallet weight: 960 kg / Bag weight: 25 kg net. Pallet weight: 1000 kg. Quantity to be loaded in a truck (82m3 ) and 40’’ marine container: 20160 kg net (21 pallets) / 20000 kg net (20 pallets).