Antioxidant; Good Chemical Resistance; Good Creep Resistance; High ESCR (Environmental Stress Cracking Resistance); High ImpactResistance
- Processing Method
Extrusion Blow Molding
Features & Benefits
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Uses
KMI 1624-GA is not intended for use in medical and pharmaceutical applications.
- Applications
HeatingOil Tanks;Industrial Packaging; Intermediate Bulk Containers Market, Industrial Packaging
Properties
- Physical Properties
- Mechanical Properties
- Typical Properties
- Thermal Properties
Value | Units | Test Method / Conditions | |
Melt Flow Rate (190°C, 21.6 Kg) | 6 | g/10 min | ISO 1133-1 |
Density | 0.945 | g/cm³ | ISO 1183-1 |
Bulk Density | min. 0.5 | g/cm³ | ISO 60 |
Intrinsic Viscosity | 370 | ml/g | ISO 1628-3 |
Value | Units | Test Method / Conditions | |
Tensile Modulus | 850 | MPa | ISO 527-1, -2 |
Tensile Stress at Yield | 24 | MPa | ISO 527-1, -2 |
Tensile Strain at Yield | 10 | % | ISO 527-1, -2 |
FNCT (3.5 MPa, 2% Arkopal N100, 80°C) | 60 | Hrs | ISO 16770 |
Value | Units | Test Method / Conditions | |
Ball Indentation Hardness (H 132/30) | 40 | MPa | ISO 2039-1 |
Melt Temperature | 180 - 220 | °C | - |
Melt Flow Rate (190°C, 5.0 kg) | 0.35 | g/10min | ISO 1133-1 |
Value | Units | Test Method / Conditions | |
Vicat Softening Temperature (A/50 N) | 125 | °C | ISO 306 |
Vicat Softening Temperature (B50) | 75 | °C | ISO 306 |
Deflection Temperature Under Load (0.45 MPa, Unannealed) | 70 | °C | ISO 75B-1, -2 |
Deflection Temperature Under Load (1.80 MPa, Unannealed) | 42 | °C | ISO 75B-1, -2 |
Melting Temperature | 42 | °C | ISO 3146 |